- Karlsson, OlovLuleå tekniska universitet,Träteknik (author)
Heat treatments of high temperature dried norway spruce boards: Saccharides and furfurals in sapwood surfaces
- Article/chapterEnglish2012
Publisher, publication year, extent ...
- 2012-03-30
- BioResources,2012
- electronicrdacarrier
Numbers
- LIBRIS-ID:oai:DiVA.org:ltu-2606
- https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-2606URI
- https://doi.org/10.15376/biores.7.2.2284-2299DOI
Supplementary language notes
- Language:English
- Summary in:English
Part of subdatabase
- SwePubSwePub
Classification
Notes
- Validerad; 2012; 20120807 (ysko)
- Carbohydrates that migrate to wood surfaces in sapwood during drying might influence properties such as mould susceptibility and colour. Sugars on the surface of Norway spruce boards during various heat treatments were studied. Samples (350mm×125mm×25mm) were double-stacked, facing sapwood-side outwards, and dried at 110°C to a target moisture content (MC) of 40%. Dried sub-samples (80 mm × 125 mm × 25 mm) were stacked in a similar way and further heated at 110°C and at 130°C for 12, 24, and 36 hours, respectively. Glucose, fructose, and sucrose as well as 5-hydroxymethylfurfural (HMF) and furfural in the sapwood surface layer of treated wood were analysed using HPLC (RI- and UV-detectors). Carbohydrates degraded to a lower extent at 110°C than at 130°C. Furfural and to a larger extent HMF increased with treatment period and temperature. Heat treatment led to a decrease in lightness and hue of the sapwood surface of sub-samples, while chroma increased somewhat. Furthermore, considerably faster degradation (within a few minutes) of the carbohydrates on the surface of the dried spruce boards was observed when single sub-samples were conductively hot pressed at 200°C. Treatment period and initial MC influenced the presence of the carbohydrates in wood surface as well as colour change (ΔE ab) of the hot pressed sub-samples.
Subject headings and genre
- TEKNIK OCH TEKNOLOGIER Industriell bioteknik Biomaterial hsv//swe
- ENGINEERING AND TECHNOLOGY Industrial Biotechnology Bio Materials hsv//eng
- Wood Physics
- Träfysik
Added entries (persons, corporate bodies, meetings, titles ...)
- Yang, QianLuleå tekniska universitet,Träteknik (author)
- Sehlstedt-Persson, MargotLuleå tekniska universitet,Träteknik(Swepub:ltu)marseh (author)
- Morén, TomLuleå tekniska universitet,Träteknik(Swepub:ltu)tomm (author)
- Luleå tekniska universitetTräteknik (creator_code:org_t)
Related titles
- In:BioResources: BioResources7:2, s. 2284-22991930-2126
Internet link
- https://ltu.diva-portal.org/smash/get/diva2:975459/FULLTEXT01.pdffulltext:print
- http://ojs.cnr.ncsu.edu/index.php/BioRes/article/download/BioRes_07_2_2284_Karlsson_YSM_Heat_Treat_Dried_Norway_Spruce/1504
- https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-2606
- https://doi.org/10.15376/biores.7.2.2284-2299
- 1 of 1
- Previous record
- Next record
- To hitlist
Find more in SwePub
- By the author/editor
- Karlsson, Olov
- Yang, Qian
- Sehlstedt-Persso ...
- Morén, Tom
- About the subject
-
- ENGINEERING AND TECHNOLOGY
- ENGINEERING AND ...
- and Industrial Biote ...
- and Bio Materials
- Articles in the publication
- BioResources
- By the university
- Luleå University of Technology
Search outside SwePub
- Extend your search to:
- Google Book Search
- Google Scholar
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.
- Copyright © LIBRIS - National Library Systems
- LIBRIS.kb.se