ZSM-5 structured catalysts coated with silicalite-1
-
Öhrman, Olov (author)
-
- Hedlund, Jonas (author)
- Luleå tekniska universitet,Industriell miljö- och processteknik
-
- Msimang, V. (author)
- Catalysis Research Unit, Department of Chemical Engineering, University of Cape Town
-
show more...
-
- Möller, V. (author)
- Catalysis Research Unit, Department of Chemical Engineering, University of Cape Town
-
Sterte, Johan (author)
-
show less...
-
(creator_code:org_t)
- Amsterdam : Elsevier, 2004
- 2004
- English.
-
In: Recent advances in the science and technology of zeolites and related materials. Part A. - Amsterdam : Elsevier. - 0444518274 ; , s. 677-684
- Related links:
-
https://urn.kb.se/re...
Abstract
Subject headings
Close
- Alumina beads were coated with ZSM-5 films ranging from 150 nm to 2300 nm ill thickness. The ZSM-5 boated alumina beads were Subsequently hydrothermally treated in a silicalite-1 synthesis solution ill two steps Whereupon a dense silicalite-1 film was formed oil top of the ZSM-5 film. The materials were tested with two probe reactions and the reactivity was compared before and after coating with silicalite-1. As expected, the para-xylene (pX) isomerization reactivity showed no change for samples with and without the top layer of silicalite-1 for equal amounts Of zeolite. Surprisingly, the triisopropylbenzene (TIPB) conversion did not decrease after the silicalite-1 film was introduced. As measured by XPS, the aluminum concentration at the Surface of the uncalcined silicalite-1 film surface was lower compared to that at the Surface of the calcined ZSM-5 film. However, after calcination the concentration of aluminum was higher at the silicalite-1 film surface than at the ZSM-5 film Surface. These results Suggest that aluminum migrates from the ZSM-5 film into the silicalite-1 film during calcination and testing which results in all active top layer.
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik -- Kemiska processer (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering -- Chemical Process Engineering (hsv//eng)
Keyword
- Chemical Technology
- Kemisk teknologi
Publication and Content Type
- ref (subject category)
- kon (subject category)
Find in a library
To the university's database