Selective etching of thermotropic liquid crystalline polyesters
-
- Hedmark, Per G. (author)
- Department of Polymer Technology, The Royal Institute of Technology, Stockholm, Sweden
-
- Jansson, Jan-Fredrik (author)
- Department of Polymer Technology, The Royal Institute of Technology, Stockholm, Sweden
-
- Hult, Anders (author)
- Department of Polymer Technology, The Royal Institute of Technology, Stockholm, Sweden
-
show more...
-
- Lindberg, Henrik (author)
- Department of Polymer Technology, The Royal Institute of Technology, Stockholm, Sweden
-
- Gedde, Ulf W. (author)
- Department of Polymer Technology, The Royal Institute of Technology, Stockholm, Sweden
-
show less...
-
(creator_code:org_t)
- Wiley, 1987
- 1987
- English.
-
In: Journal of Applied Polymer Science. - : Wiley. - 0021-8995 .- 1097-4628. ; 34:2, s. 743-762
- Related links:
-
https://urn.kb.se/re...
-
show more...
-
https://doi.org/10.1...
-
show less...
Abstract
Subject headings
Close
- DSC, IR, ESCA, macroscopic etching rate measurements, analysis of etchant solution, and electron microscopy conclusively show that n-alkylamines (ethylamine, n-propylamine, n-butylamine, and n-pentylamine) and NaOH selectively degrade (etch) the ethylene terephthalate (ET)-rich phase in glassy liquid crystalline poly(p-hydroxybenzoic acid-co-ethylene terephthalate) [P(HBA-ET)] with molar compositions 0.60:0.40 and 0.80:0.20. ESCA demonstrates the excellent selectivity of the n-alkylamine etchants in the 0.60:0.40 copolymer. The 50 Å top layer of the etched samples contains 95 mol% HBA. Treatment with H2SO4 and NH3 gives ambiguous results, and these compounds are not suitable as etchants. It is demonstrated by electron microscopy on the 0.60:0.40 copolymer, in accordance with earlier reports by Joseph et al.,5-8 that the ET-rich phase is discontinuous (1-2 m spheres) and surrounded by an HBA-rich matrix. SEM is a useful tool for characterization of this morphology. However, both phases have a substracture which is revealed only by TEM. The morphology of the 0.80:0.20 copolymer is fine-textured, which means that SEM is a less suitable method for the characterization of etched samples.
- DSC, IR, ESCA, macroscopic etching rate measurements, analysis of etchant solution, and electron microscopy conclusively show that n-alkylamines (ethylamine, n-propylamine, n-butylamine, and n-pentylamine) and NaOH selectively degrade (etch) the ethylene terephthalate (ET)-rich phase in glassy liquid crystalline poly(p-hydroxybenzoic acid-co-ethylene terephthalate) [P(HBA-ET)] with molar compositions 0.60:0.40 and 0.80:0.20. ESCA demonstrates the excellent selectivity of the n-alkylamine etchants in the 0.60:0.40 copolymer. The 50 Å top layer of the etched samples contains 95 mol% HBA. Treatment with H2SO4 and NH3 gives ambiguous results, and these compounds are not suitable as etchants. It is demonstrated by electron microscopy on the 0.60:0.40 copolymer, in accordance with earlier reports by Joseph et al.,5-8 that the ET-rich phase is discontinuous (1-2 m spheres) and surrounded by an HBA-rich matrix. SEM is a useful tool for characterization of this morphology. However, both phases have a substracture which is revealed only by TEM. The morphology of the 0.80:0.20 copolymer is fine-textured, which means that SEM is a less suitable method for the characterization of etched samples.
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Industriell bioteknik -- Biomaterial (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Industrial Biotechnology -- Bio Materials (hsv//eng)
Keyword
- Träfysik
- Wood Physics
Publication and Content Type
- ref (subject category)
- art (subject category)
Find in a library
To the university's database