A modified specimen...
-
Sandinge, AnnaRISE,Brandteknik,DTU Technical University of Denmark, denmark
(author)
A modified specimen holder for cone calorimeter testing of composite materials to reduce influence from specimen edges
- Article/chapterEnglish2022
Publisher, publication year, extent ...
-
2021-02-16
-
John Wiley and Sons Ltd,2022
-
printrdacarrier
Numbers
-
LIBRIS-ID:oai:DiVA.org:ri-52907
-
https://urn.kb.se/resolve?urn=urn:nbn:se:ri:diva-52907URI
-
https://doi.org/10.1002/fam.2949DOI
Supplementary language notes
-
Language:English
-
Summary in:English
Part of subdatabase
Classification
-
Subject category:ref swepub-contenttype
-
Subject category:art swepub-publicationtype
Notes
-
Funding details: Seventh Framework Programme, FP7, 246037; Funding details: Seventh Framework Programme, FP7; Funding details: Horizon 2020, 723246; Funding text 1: The research reported here was conducted within the EU project FIRE‐RESIST which received funding from the European Community's Seventh Framework Programme (FP7/2007‐2013) under grant agreement No. 246037. The research is also a part of the RAMSSES project which has received funding under the European Union's Horizon 2020 research and innovation programme under the grant agreement No 723246.
-
ISO 5660-1 specifies the cone calorimeter method for characterizing the ignition and surface burning behavior of materials. The specimen is irradiated through a square opening in the frame of the specimen holder. The frame is intended to protect the edges of the specimen from irradiation but covers the edges with only a few mm. In tests with products such as composite laminates and sandwich wall panels, the production of pyrolysis gases from the edges and, in many cases, burning have been observed. Early contribution from the edges in the test is not representative for surface burning. A modified specimen holder was developed with a larger specimen size to allow better protection of the edges. The opening for exposure to irradiance of the retainer frame is circular and of the same area as that of the original frame. The distance between the exposed surface and the specimen edges is larger in order to prevent early exposure of edges. Tests using the standard specimen holder resulted in pyrolysis and burning from edges that took place outside of the specimen holder. Comparative tests using the modified specimen holder showed that it prevented the exposure and pyrolysis from edges for an extended time. However, the influence on ignition time and peak heat release due to the increased size of the modified specimen holder has not been characterized fully, and test results should not be used for direct comparison with those of the standard holder.
Subject headings and genre
Added entries (persons, corporate bodies, meetings, titles ...)
-
Blomqvist, PerRISE,Brandteknik(Swepub:ri)PerBlom@ri.se
(author)
-
Rahm, MichaelRISE,Säkerhetsforskning
(author)
-
RISEBrandteknik
(creator_code:org_t)
Related titles
-
In:Fire and Materials: John Wiley and Sons Ltd46:1, s. 80-0308-05011099-1018
Internet link
Find in a library
To the university's database