Phase formation, crystal structures and magnetic properties of perovskite-type phases in the system La2Co1+z(MgxTi1-x)1-zO6

• Perovskite-type cobaltates in the system La(2)Co(1+z) (Mg(x)Ti(1-x))(1-z)O(6) were studied for z=0 <= x <= 0.6 and 0 <= x <= 0.9, using X-ray and neutron powder diffraction, electron diffraction (ED), magnetic susceptibility measurements and X-ray absorption near-edge structure (XANES) spectroscopy. The samples were synthesised using the citrate route in air at 1350 degrees C. The space group symmetry of the structure changes from P2(1)/n via Pbnm to R (3) over barc with both increasing Mg content and increasing Co content. The La(2)Co(Mg(x)Ti(1-x))O(6) (z=0) compounds show anti-ferromagnetic couplings of the magnetic moments for the Co below 15 K for x=0, 0.1 and 0.2. XANES spectra show for the compositions 0 <= x <= 0.5 a linear decrease in the L(3)/(L(3)+ L(2))Co-L(2.3) edge branching ratio with x, in agreement with a decrease of the average Co ion spin-state, from a high-spin to a lower-spin-state, with decreasing nominal Co(2+) ion content.

Subject headings

NATURVETENSKAP  -- Kemi -- Oorganisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)

NATURVETENSKAP  -- Kemi -- Fysikalisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Physical Chemistry (hsv//eng)

NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)

Keyword

Cobaltates

perovskite

X-ray diffraction

neutron diffraction

magnetic susceptibility

electron diffraction

XANES

Solid state chemistry

Fasta tillståndets kemi

Inorganic Chemistry

oorganisk kemi

Materials Chemistry

materialkemi

Publication and Content Type

ref (subject category)

art (subject category)