High pressure and high temperature induced polymerization of C60 nanotubes

• C60 nanotubes with outer diameters ranging from 400–800 nm were polymerized at 1.5 GPa, 573 K and 2.0 GPa, 700 K, respectively. Raman and photoluminescence spectroscopy were employed to characterize the polymeric phases of the treated samples. Both Raman and photoluminescence spectra showed that the C60 nanotubes transformed into the dimer and orthorhombic phases under the two different conditions, respectively. The photoluminescence peaks were tuned from visible to near infrared range. Comparative studies indicated that C60 nanotubes were more difficult to polymerize than bulk C60 material under the same conditions due to the nanoscale size effect in the C60 nanotubes.

Subject headings

NATURVETENSKAP  -- Fysik -- Den kondenserade materiens fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences -- Condensed Matter Physics (hsv//eng)

Keyword

Fullerenes

C60

nanotubes

high pressure

polymerization

Raman scattering

X-ray diffraction

linear chains

dimers

photoluminescence

Condensed matter physics

Kondenserade materiens fysik

fysik

Physics

Publication and Content Type

ref (subject category)

art (subject category)