Microstructural Investigation of SiOx Thin Films Grown by Reactive Sputtering on (001) Si Substrates

• In the Current Study, the Structural Characteristics of Siox Thin Films Grown by Magnetron Sputtering on Si Substrates Are Reported. High Resolution Transmission Electron Microscopy Revealed the Formation of Amorphous Siox Films for the as-Deposited Samples, as Well as the Ones Annealed in Ambient Air for 30 Min at 950oC and of Si Nanocrystals, Embedded in Amorphous Siox, after Ar Annealing for 1-4 Hours at 1000oC. the Nanocrystals, with Sizes up to 6 Nm, Predominately Exhibit {111} Lattice Planes. Energy-Dispersive X-Ray Analysis Showed that the Si/O Ratio Is between 0.5-1, I.e. the Amorphous Films Comprise of a Mixture of Sio2 and Sio. Phase Images and Corresponding Strain Maps Created Using Fourier Filtering Revealed a Uniform Contrast in the Nanocrystals, which Shows that the Si Lattice Constant Does Not Vary Significantly. the Residual Strain Variations, around 4%, May Account for the Possible Existence of a Small Percentage of Highly Disordered Si or Siox Residual Clusters inside the Regular Si Matrix, in Full Agreement with Photoluminescence Measurements Performed on the same Materials.

Subject headings

NATURVETENSKAP  -- Fysik -- Den kondenserade materiens fysik (hsv//swe)

NATURAL SCIENCES  -- Physical Sciences -- Condensed Matter Physics (hsv//eng)

Keyword

Physics

Fysik

Materiefysik

Physics of Matter

Publication and Content Type

ref (subject category)

art (subject category)