Understanding microstructure-mechanical properties relationship in ZrO2-SiO2 nanocrystalline glass-ceramics : The effect of ZrO2 content

• The content of crystalline phase plays a significant role in manipulating the microstructure and mechanical properties of glass-ceramics. This study aims at exploring the optimum content of crystalline phase in ZrO2-SiO2 nanocrystalline glass-ceramics (NCGCs) in terms of obtaining the highest mechanical properties. To this end, the mechanical properties of ZrO2-SiO2 NCGCs with 70 mol%, 75 mol%, 80 mol% ZrO2 were tested and compared with those of the previously prepared NCGCs with ZrO2 content ranging from 35 mol% to 65 mol%. Results showed that 65 mol% was the optimum content of ZrO2 in terms of obtaining the highest flexural strength. The flexural strength of NCGCs with ZrO2 content over 65 mol% was lower than that of the NCGCs with 65 mol% ZrO2. This was because the NCGC with 65 mol% ZrO2 had a homogenous microstructure, with ZrO2 nano crystallites homogeneously distributed in an amorphous SiO2 matrix. Whereas, when ZrO2 content was increased to 75 mol%, ZrO2 nanocrystallites were not homogeneously distributed in the SiO2 matrix anymore. The formation of SiO2 "holes/canyon " due to ZrO2 grain coalescence resulted in the decrease of flexural strength. The fracture mechanism and wear properties of the NCGCs were also investigated.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Keramteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Ceramics (hsv//eng)

Keyword

ZrO2-SiO2

Nanocrystalline glass-ceramics

Fractography

Microstructure

Mechanical properties

Publication and Content Type

ref (subject category)

art (subject category)