Injectable bone cements for vertebroplasty studied in sheep vertebrae with electron microscopy

• Vertebral compression fractures were simulated by making a hole into sheep vertebrae and by injecting a stabilizing material. The injectable bio-ceramic Xeraspine™ was evaluated together with a commercially available PMMA (Vertebroplastic™) as the reference material. The Vertebrae were harvested after 7 days and prepared for microscopy. The samples were deposited with gold on the surface and thereafter subjected to SEM and EDX analysis. It was found that the Xeraspine-bone interface was composed of a mixture of elements. The Vertebroplastic implant was embedded in a carbon containing tissue, likely a soft tissue capsule. The Xeraspine sample was subjected to high resolution analysis in the TEM combined with EDX measurements. The TEM sample was prepared with a novel technique for preparation of the tissue-material interface (FIB). In the TEM analysis it was found that the interface region consists of ZrO2 together with a mixture possibly consisting of katoite and apatite formed during setting and/or originating from the boneapatite.

Subject headings

MEDICIN OCH HÄLSOVETENSKAP  -- Klinisk medicin (hsv//swe)

MEDICAL AND HEALTH SCIENCES  -- Clinical Medicine (hsv//eng)

MEDICIN OCH HÄLSOVETENSKAP  -- Medicinsk bioteknologi -- Biomaterialvetenskap (hsv//swe)

MEDICAL AND HEALTH SCIENCES  -- Medical Biotechnology -- Biomaterials Science (hsv//eng)

Publication and Content Type

ref (subject category)

art (subject category)