Mechanical degradation and changes in conformation of hydrophobically modified starch
-
- Nilsson, Lars (author)
- Lund University,Lunds universitet,Livsmedelsteknik,Avdelningen för livsmedel och läkemedel,Institutionen för processteknik och tillämpad biovetenskap,Institutioner vid LTH,Lunds Tekniska Högskola,Department of Food Technology, Engineering and Nutrition,Division of Food and Pharma,Department of Process and Life Science Engineering,Departments at LTH,Faculty of Engineering, LTH
-
- Leeman, Mats (author)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
- Wahlund, Karl-Gustav (author)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
show more...
-
- Bergenståhl, Björn (author)
- Lund University,Lunds universitet,Livsmedelsteknik,Avdelningen för livsmedel och läkemedel,Institutionen för processteknik och tillämpad biovetenskap,Institutioner vid LTH,Lunds Tekniska Högskola,Department of Food Technology, Engineering and Nutrition,Division of Food and Pharma,Department of Process and Life Science Engineering,Departments at LTH,Faculty of Engineering, LTH
-
show less...
-
(creator_code:org_t)
- 2006-08-12
- 2006
- English.
-
In: Biomacromolecules. - : American Chemical Society (ACS). - 1526-4602 .- 1525-7797. ; 7:9, s. 2671-2679
- Related links:
-
http://dx.doi.org/10...
-
show more...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
show less...
Abstract
Subject headings
Close
- In this paper, we study the mechanical degradation and changes in conformation of a branched ultrahigh molar mass biomacromolecule, hydrophobically modified starch, as caused by high-pressure homogenization. The characterization was performed with asymmetrical flow field-flow fractionation (AsFlFFF) with multiangle light scattering (MALS) and refractive index detection. The starch which had been chemically modified with octenyl succinate anhydride (OSA) proved to be very large and polydisperse. Upon high-pressure homogenization, the molar mass and rms radius (r(rms)) decreased, and the extent of these changes was related to the turbulent flow conditions during homogenization. The treatment also induced an increase and scaling with size in the apparent density of the macromolecules. To further study the changes in conformation, it was necessary to calculate the hydrodynamic radii (r(h)). This can be determined numerically from the elution times in the analysis and the flow conditions in the AsFlFFF channel. The results showed that the treatment can cause a dramatic decrease in the quotient between r(rms) and r(h), suggesting major conformational changes. These results together could be interpreted as degradation and "crumpling" of the macromolecule, which would give a decrease in rrms and an increase in apparent density, together with a "fraying" of more outer parts of the macromolecule, which could give rise to the increase in r(h).
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Annan teknik -- Livsmedelsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Other Engineering and Technologies -- Food Engineering (hsv//eng)
- NATURVETENSKAP -- Kemi -- Analytisk kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Analytical Chemistry (hsv//eng)
Publication and Content Type
- art (subject category)
- ref (subject category)
Find in a library
To the university's database