X-ray absorption study of oxygen in the high-Tc superconductor Bi2Sr2CaCu2O8 near the interfaces to Cu, Ag and Au
-
Qvarford, M. (author)
-
- Söderholm, S. (author)
- ABB Corporate Research, Sweden
-
- Tjernberg, O. (author)
- KTH Royal Institute of Technology
-
show more...
-
Chiaia, G. (author)
-
- Nylén, H. (author)
- Lund University,Lunds universitet,Synkrotronljusfysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Synchrotron Radiation Research,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
-
- Nyholm, R. (author)
- Lund University,Lunds universitet,Synkrotronljusfysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Synchrotron Radiation Research,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
-
- Lindau, I. (author)
- Lund University,Lunds universitet,Synkrotronljusfysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Synchrotron Radiation Research,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
-
- Karlsson, U. O. (author)
- KTH,KTH Royal Institute of Technology,Skolan för informations- och kommunikationsteknik (ICT),Materialfysik
-
- Bernhoff, H. (author)
- ABB Corporate Research, Sweden
-
show less...
-
(creator_code:org_t)
- Elsevier BV, 1996
- 1996
- English 8 s.
-
In: Physica C: Superconductivity and its Applications. - : Elsevier BV. - 0921-4534 .- 1873-2143. ; 265:1-2, s. 113-120
- Related links:
-
https://lup.lub.lu.s...
-
show more...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
show less...
Abstract
Subject headings
Close
- The influence on O 2p holes in single crystalline Bi2Sr2CaCu2O8 upon the interface formation to Cu, Ag and Au has been studied by O K edge X-ray absorption measurements. It was found that Cu reduces the amount of doping induced O 2p holes significantly in the vicinity of the interface, whereas Ag and Au gave a much smaller reduction of these states. Photoemission spectra confirmed previous findings that Cu causes a strong chemical reaction at the Bi-O surface of Bi2Sr2CaCu2O8, in contrast to Ag and Au which induced only a minimal reaction. The results support the opinion that the Bi-O layers are essential for the doping of the Cu-O2 layers in Bi2Sr2CaCu2O8.
Keyword
- Cu-O planes
- Hole concentration
- Metal overlayer
- Normal state properties
- XAFS
Publication and Content Type
- art (subject category)
- ref (subject category)
Find in a library
To the university's database