A Study of Spreading of Vanadia on Titania Polymorphs Using Mechanical Mixtures
-
- Sanati, Mehri (author)
- Lund University,Lunds universitet,Ergonomi och aerosolteknologi,Institutionen för designvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Ergonomics and Aerosol Technology,Department of Design Sciences,Departments at LTH,Faculty of Engineering, LTH
-
- Andersson, Arne (author)
- Lund University,Lunds universitet,Avdelningen för kemiteknik,Institutionen för processteknik och tillämpad biovetenskap,Institutioner vid LTH,Lunds Tekniska Högskola,Division of Chemical Engineering,Department of Process and Life Science Engineering,Departments at LTH,Faculty of Engineering, LTH
-
- Wallenberg, Reine (author)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
show more...
-
Guczi et al, L (editor)
-
show less...
-
(creator_code:org_t)
- 1993
- 1993
- English.
-
In: New Frontiers in Catalysis (Studies in Surface Science and Catalysis ). - 0167-2991. ; 75, s. 1755-1758
- Related links:
-
http://dx.doi.org/10...
-
show more...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
show less...
Abstract
Subject headings
Close
- Mechanical mixtures of V2O5 and each of the three titania polymorphs TiO2(B), anatase and rutile were heated in air at 450°C. Spreading of vanadia was found to occur on all three polymorphs. After 36 hours of heating, coverage with interacting vanadia (the part that is insoluble in aq. NH3) on TiO2(B), anatase and rutile, respectively, was 54, 48 and 38 % of a theoretical monolayer. Raman spectra confirmed spreading and interaction. HREM images revealed no formation of multilayers of vanadia on titania. Use of the monolayer catalysts for toluene ammoxidation indicated their activity for benzonitrile formation to vary with respect to support in the order TiO2(B) > anatase > rutile.
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Produktionsteknik, arbetsvetenskap och ergonomi (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Production Engineering, Human Work Science and Ergonomics (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering (hsv//eng)
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Publication and Content Type
- kon (subject category)
- ref (subject category)
Find in a library
To the university's database