Search: onr:"swepub:oai:research.chalmers.se:1ff66a60-ff6a-45c9-b088-9278aff3d1bb" >
The efficiency of H...
Abstract
Subject headings
Close
- Different post‐weld treatment methods have been developed to enhance the fatigue strength of welded steel structures and extend the service lives of their components. High‐frequency mechanical impact (HFMI) treatment and tungsten inert gas (TIG) remelting are two methods that have attracted considerable interest in recent decades. This paper presents the results of a study of fatigue life extension for pre‐fatigued welded steel details which can be achieved using HFMI treatment and TIG remelting. More than 250 fatigue test results were collected – including different details such as butt welds, longitudinal attachments, transverse attachments and cover plate attachments. HFMI treatment was found to extend the life considerably when the specimens treated were free from cracks or when existing cracks were < 2.25 mm deep. TIG remelting could extend fatigue lives even with cracks > 4 mm deep. In comparison to TIG remelting, HFMI treatment results in a longer fatigue life extension for pre‐fatigued details, provided existing cracks are < 2.25 mm deep. Regarding TIG remelting, the depth of possible remaining cracks was found to be a substantial parameter when assessing the degree of life extension.
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Samhällsbyggnadsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Civil Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
Keyword
- allowable crack size
- analysis and design
- TIG remelting
- pre‐fatigue
- Steel bridges
- experiments
- high‐frequency mechanical impact
- fatigue life extension
Publication and Content Type
- art (subject category)
- ref (subject category)
Find in a library
To the university's database