The effect of crystallographic orientation on solid metal induced embrittlement of Ti-6Al-1Mo-1V in contact with copper

• Solid metal induced embrittlement (SMIE) occurs when a metal experiences tensilestress and is in contact with another metal with lower melting temperature. SMIE is believed tobe a combined action of surface self-diffusion of the embrittling species to the crack tip andadsorption of the embrittling species at the crack tip, which weakens the crack tip region. In thepresent study, both SMIE of the near alpha alloy Ti-8Al-1Mo-1V in contact with copper and itsinfluence by crystallographic orientation have been studied. U-bend specimens coated withcopper were heat treated at 480°C for 8 hours. One of the cracks was examined in detail usingelectron backscatter diffraction technique. A preferable crack path was found along high anglegrain boundaries with grains oriented close to [0001] in the crack direction; this indicates thatthere is a connection between the SMIE crack characteristics and the crystallographicorientation.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Maskinteknik -- Teknisk mekanik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering -- Applied Mechanics (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

Keyword

titan

metal induced embrittlement (MIE)

EBSD

crystallographic orientation

Materialteknik

Publication and Content Type

kon (subject category)

ref (subject category)