Effect of Direct Energy Deposition Process Parameters on Single-Track Deposits of Alloy 718
- Artikel/kapitelEngelska2020
Förlag, utgivningsår, omfång ...
-
2020-01-07
-
MDPI AG,2020
-
electronicrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:hv-14922
-
https://urn.kb.se/resolve?urn=urn:nbn:se:hv:diva-14922URI
-
https://doi.org/10.3390/met10010096DOI
-
https://urn.kb.se/resolve?urn=urn:nbn:se:hj:diva-47590URI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
The effect of three important process parameters, namely laser power, scanning speed and laser stand-off distance on the deposit geometry, microstructure and segregation characteristics in direct energy deposited alloy 718 specimens has been studied. Laser power and laser stand-off distance were found to notably affect the width and depth of the deposit, while the scanning speed influenced the deposit height. An increase in specific energy conditions (between 0.5 J/mm2 and 1.0 J/mm2) increased the total area of deposit yielding varied grain morphologies and precipitation behaviors which were comprehensively analyzed. A deposit comprising three distinct zones, namely the top, middle and bottom regions, categorized based on the distinct microstructural features formed on account of variation in local solidification conditions. Nb-rich eutectics preferentially segregated in the top region of the deposit (5.4–9.6% area fraction, Af) which predominantly consisted of an equiaxed grain structure, as compared to the middle (1.5–5.7% Af) and the bottom regions (2.6–4.5% Af), where columnar dendritic morphology was observed. High scan speed was more effective in reducing the area fraction of Nb-rich phases in the top and middle regions of the deposit. The <100> crystallographic direction was observed to be the preferred growth direction of columnar grains while equiaxed grains had a random orientation.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Hurtig, Kjell,1960-Högskolan Väst,Avdelningen för svetsteknologi (SV),PTW,Department of Engineering Science, University West, Trollhättan, Sweden(Swepub:hv)tkh
(författare)
-
Joshi, Shrikant V.,1960-Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW,Department of Engineering Science, University West, Trollhättan, Sweden(Swepub:hv)shrjos
(författare)
-
Andersson, Joel,1981-Högskolan Väst,Avdelningen för svetsteknologi (SV),PTW,Department of Engineering Science, University West, Trollhättan, Sweden(Swepub:hv)joan0056
(författare)
-
Ghassemali, Ehsan,1983-Jönköping University,JTH, Material och tillverkning(Swepub:hj)GhaEhs
(författare)
-
Högskolan VästAvdelningen för svetsteknologi (SV)
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Metals: MDPI AG10:1, s. 01-162075-4701
Internetlänk
Hitta via bibliotek
-
Metals
(Sök värdpublikationen i LIBRIS)
Till lärosätets databas