Mistri, MourmitaAdvanced Nanoengineering Materials Laboratory, Materials Science Programme, Indian Institute of Technology Kanpur, Uttar Pradesh 208016, India (IND)
(författare)
Tribomechanical insight into carbide-laden hybrid suspension-powder plasma-sprayed Tribaloy T400 composite coatings
- Artikel/kapitelEngelska2020
Förlag, utgivningsår, omfång ...
-
Elsevier BV,2020
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:hv-15733
-
https://urn.kb.se/resolve?urn=urn:nbn:se:hv:diva-15733URI
-
https://doi.org/10.1016/j.surfcoat.2020.125957DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Funders;DST (Department of Science and Technology), Govt. of India(DST/SJF/ETA-02-2016-17)
-
Tribaloy T400 (CoCrMoSi) caters to heavy-duty industrial tribological demands, but exhibits low fracture toughness with compromised resistance to crack propagation owing to the disparity in % Laves phases. In response to this limitation, hybrid suspension-powder plasma-sprayed novel Cr3C2 (d50 of 3.8 ÎŒm)/TiC (d50 of 2.2 ÎŒm) reinforced T400 (average powder size of 10â45 ÎŒm) coatings are deposited on grit-blasted SSAB Domex®350 LA steel. Continuous, adherent and co-existing lamellar T400-carbide coatings of 100 ÎŒm thickness were revealed in microstructure analysis. Intermetallic CoMoSi/Co3Mo2Si Laves and eutectic Co7Mo6/Co2Mo7 phases in T400 in addition to Cr3C2/TiC characteristic phases are confirmed via X-ray diffraction study. T400-Cr3C2 and T400-TiC have exhibited enhancement in elastic modulus (E) by 39%, and 36%, Vickers hardness (Hv) by 68%, and 82.5%; which consequently elucidates the augmentation in plasticity index (re) by 15.7% and 26.7%, and the drop in maximum displacement amplitude (hmax) by 14.9% and 19.8%, respectively, in T400-Cr3C2 and T400-TiC with reference to T400 (E of 135.2 GPa, Hv of 6.3 GPa, re = 0.318, and hmax = 1947 nm). A subsequent surmised fretting Hertzian contact diameter in T400-Cr3C2 ( 95.43 ÎŒm)/T400-TiC ( 96.1 ÎŒm) evaluated against T400 ( 106.9 ÎŒm) from optical profilometry indicates an improved damage tolerance. A contact area-based wear model, proposed herein to assess wear on a rough surface, further justifies the wear characteristics. Furthermore, synergistic L929 cell viability is recorded in T400-Cr3C2 (by 46%) and T400-TiC (by 30%) when compared with the control (+ve) disk. To conclude, suspension-powder plasma-sprayed T400-Cr3C2/T400-TiC composite coatings allude potential application in wear-resistant articulating surfaces by eliciting significantly enhanced micro-hardness through refined microstructure retention, improved fretting wear resistance by forming protective tribofilm, and augmented cellular response. © 2020 Elsevier B.V.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Joshi, Shrikant V.,1960-Högskolan Väst,Forskningsmiljön produktionsteknik(PTW),PTW(Swepub:hv)shrjos
(författare)
-
Kar, Kamal K.Advanced Nanoengineering Materials Laboratory, Materials Science Programme, Indian Institute of Technology Kanpur, Uttar Pradesh 208016, India; Advanced Nanoengineering Materials Laboratory, Mechanical Engineering, Indian Institute of Technology Kanpur, Uttar Pradesh 208016, India (IND)
(författare)
-
Balani, KanteshMaterials Science and Engineering, Indian Institute of Technology Kanpur, Uttar Pradesh 208016, India (IND)
(författare)
-
Advanced Nanoengineering Materials Laboratory, Materials Science Programme, Indian Institute of Technology Kanpur, Uttar Pradesh 208016, India (IND)Forskningsmiljön produktionsteknik(PTW)