Carbide-laden coatings deposited using a hand-held high-velocity air-fuel (HVAF) spray gun
-
- Baiamonte, Lidia (författare)
- Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),LIMS, INSTM Reference Laboratory for Engineering of Surface reatments, Department of Chemical Engineering Materials Environment, Sapienza University of Rome, Rome, ITA,PTW,University West,Universita degli Studi di Roma la Sapienza,Sapienza University of Rome
-
- Björklund, Stefan, 1969- (författare)
- Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW,University West
-
- Mulone, Antonio, 1989 (författare)
- Department of Industrial and Materials Science, Chalmers University of Technology, Gothenburg,Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
- Klement, Uta, 1962 (författare)
- Department of Industrial and Materials Science, Chalmers University of Technology, Gothenburg,Chalmers tekniska högskola,Chalmers University of Technology
-
- Joshi, Shrikant V., 1960- (författare)
- Högskolan Väst,Avdelningen för avverkande och additativa tillverkningsprocesser (AAT),PTW,University West
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2021
- 2021
- Engelska.
-
Ingår i: Surface & Coatings Technology. - : Elsevier BV. - 0257-8972 .- 1879-3347. ; 406
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
https://research.cha...
-
https://research.cha...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- Driven by sustainability and cost considerations, there is growing interest in power generation utilizing renewable sources, especially biomass and waste. While premature degradation of power plant components due to corrosion is well-known, erosion can be a dominant damage mechanism in plants that use “pure” biomass with less corrosive elements like Cl, K, etc. Circulating fluidized bed (CFB) parts are prone to erosion-driven damage and demand periodic re-protection or replacement. In response to the above, this preliminary study evaluates a selection of complex carbide-based coatings to enhance protection against erosion to prolong service life of boiler components. Recognizing on-site coating requirements of real boiler applications, a specific focus is on evaluating performance of a hand-held high-velocity air-fuel (HVAF) spray gun and compare it with the current state-of-the-art high-velocity oxy-fuel (HVOF) deposition. Coatings developed by the above routes have been characterized with microstructural analyses, and their performance evaluated and ranked in an air-jet erosion rig at various impact angles.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- Hand-held HVAF
- Cermet
- Chromium carbide
- HVOF
- Dry particle erosion
- Microstructural characterization
- Production Technology
- Produktionsteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas