The 475 degrees C embrittlement in Fe-20Cr and Fe-20Cr-X (X=Ni, Cu, Mn) alloys studied by mechanical testing and atom probe tomography
- Artikel/kapitelEngelska2013
Förlag, utgivningsår, omfång ...
-
Elsevier BV,2013
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:kth-124438
-
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-124438URI
-
https://doi.org/10.1016/j.msea.2013.03.016DOI
-
https://urn.kb.se/resolve?urn=urn:nbn:se:ri:diva-12815URI
-
https://research.chalmers.se/publication/179785URI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
QC 20130710
-
In the present work the 475 degrees C embrittlement in binary Fe-Cr and ternary Fe-Cr-X (X=Ni, Cu and Mn) alloys have been investigated. The mechanical properties were evaluated using microhardness and impact testing, and the structural evolution was evaluated using atom probe tomography (APT). The APT results after aging at 500 degrees C for 10 h clearly showed that both Ni and Mn accelerate the ferrite decomposition. No evident phase separation of either the Fe-20Cr or Fe-20Cr-1.5Cu samples was detected after 10 h of aging and thus no conclusions on the effect of Cu can be drawn. Cu clustering was however found in the Fe-20Cr-1.5Cu sample after 10 h aging at 500 degrees C. The mechanical property evolution was consistent with the structural evolution found from APT. Samples aged at 450 and 500 degrees C all showed increasing hardness and decreasing impact energy. The embrittlement was observed to take place mainly during the first 10 h of aging and it could primarily be attributed to phase separation, but also substitutional solute clustering and possibly carbon and nitrogen segregation may contribute in a negative way.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Huyan, FeiKTH,Metallografi,KTH Royal Institute of Technology, Sweden,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)(Swepub:kth)u109szv3
(författare)
-
Zhou, JingKTH,Metallografi,KTH Royal Institute of Technology, Sweden,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)(Swepub:kth)u1ce11k1
(författare)
-
Wessman, StenRISE,KTH,Metallografi,KIMAB(Swepub:kth)u1ybfvsy
(författare)
-
Thuvander, Mattias,1968Chalmers University of Technology, Sweden,Chalmers tekniska högskola(Swepub:cth)matthu
(författare)
-
Odqvist, JoakimKTH,Metallografi,KTH Royal Institute of Technology, Sweden,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)(Swepub:kth)u1dxktvd
(författare)
-
KTHMetallografi
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Materials Science & Engineering: Elsevier BV574, s. 123-1290921-50931873-4936
Internetlänk
Hitta via bibliotek
Till lärosätets databas