Phosphorus removal by slag depends on its mineralogical composition: A comparative study of AOD and EAF slags
-
- Renman, Gunno (författare)
- KTH,Hållbar utveckling, miljövetenskap och teknik
-
- Zuo, Minyu (författare)
- KTH,Hållbar utveckling, miljövetenskap och teknik
-
- Gustafsson, Jon Petter, 1964- (författare)
- Swedish University of Agricultural Sciences,Sveriges lantbruksuniversitet,KTH,Hållbar utveckling, miljövetenskap och teknik,Institutionen för mark och miljö,Department of Soil and Environment,Royal Institute of Technology (KTH)
-
visa fler...
-
- Klysybun, Wantana (författare)
- Synchrotron Light Research Institute, 111 University Avenue, Muang District, Nakorn, Ratchasima, 30000, Thailand
-
visa färre...
-
(creator_code:org_t)
-
- Elsevier, 2018
- 2018
- Engelska.
-
Ingår i: Journal of Water Process Engineering. - : Elsevier. - 2214-7144. ; 25, s. 105-112
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
https://res.slu.se/i...
-
visa färre...
Abstract
Ämnesord
Stäng
- Electric arc furnace slag (EAF) and argon oxygen decarburization slag (AOD) were investigated in column experiments to determine the effect of mineralogical composition on their P removal performance and lifespan. Polyethylene glycol (PEG) and NaOH solutions were used for pretreatment of the slags to adjust their dissolution properties. The modified slags exhibited better P removal performance at the beginning of the experiment, but had shorter lifespan than the unmodified slags. AOD and EAF modified with PEG and NaOH achieved 100% P removal during the first 84 and 60 pore volumes, respectively, which were ≥20 pore volumes longer than virgin AOD and EAF. However, virgin EAF and AOD both had a P removal efficiency above 90% during the first 280 pore volumes. Possibly, soluble minerals such as free lime are lost during the modification step, causing a decreased long-term P removal capacity. The XRD results showed that the high P removal ability of AOD and EAF was attributed to the dissolution of beta dicalcium silicate (β-C2) and gamma dicalcium silicate (γ-C2S), which were dominant mineral phases in the slags. Results from SEM-EDS analysis revealed significant P accumulation on the slag surface. Cracks on the EAF slag surface contributed to its longer lifespan. Analysis with P K-edge XANES spectroscopy showed that the P retained on the slag surface was dominated by amorphous calcium phosphate, with a substantial amount of carbonate apatite (around 30%). Amorphous calcium phosphate was transformed to crystalline apatite as the slag aged with column operating time.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Miljöbioteknik -- Vattenbehandling (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Environmental Biotechnology -- Water Treatment (hsv//eng)
Nyckelord
- Land and Water Resources Engineering
- Mark- och vattenteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas