Improved Cellulose Nanofibril Dispersion in Melt-Processed Polycaprolactone Nanocomposites by a Latex-Mediated Interphase and Wet Feeding as LDPE Alternative
-
- Lo Re, Giada, PhD, 1971- (författare)
- KTH,Biokompositer
-
- Engström, Joakim (författare)
- KTH,Ytbehandlingsteknik,Wallenberg Wood Science Center
-
- Wu, Qiong (författare)
- KTH,Biokompositer
-
visa fler...
-
- Malmström, Eva (författare)
- KTH,Wallenberg Wood Science Center
-
- Gedde, Ulf W. (författare)
- KTH,Polymera material
-
- Olsson, Richard (författare)
- KTH,Polymera material
-
- Berglund, Lars, 1979- (författare)
- KTH,Biokompositer,Ytbehandlingsteknik
-
visa färre...
-
(creator_code:org_t)
- 2018-05-14
- 2018
- Engelska.
-
Ingår i: ACS Applied Nano Materials. - : American Chemical Society (ACS). - 2574-0970. ; 1:6, s. 2669-2677
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- This work reports the development of a sustainable and green one-step wet-feeding method to prepare tougher and stronger nanocomposites from biodegradable cellulose nanofibrils (CNF)/polycaprolactone (PCL) constituents, compatibilized with reversible addition fragmentation chain transfer-mediated surfactant-free poly(methyl methacrylate) (PMMA) latex nanoparticles. When a PMMA latex is used, a favorable electrostatic interaction between CNF and the latex is obtained, which facilitates mixing of the constituents and hinders CNF agglomeration. The improved dispersion is manifested in significant improvement of mechanical properties compared with the reference material. The tensile tests show much higher modulus (620 MPa) and strength (23 MPa) at 10 wt % CNF content (compared to the neat PCL reference modulus of 240 and 16 MPa strength), while maintaining high level of work to fracture the matrix (7 times higher than the reference nanocomposite without the latex compatibilizer). Rheological analysis showed a strongly increased viscosity as the PMMA latex was added, that is, from a well-dispersed and strongly interacting CNF network in the PCL.
Ämnesord
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas