Analysis of O-Ring Seal Failure under Static Conditions and Determination of End-of-Lifetime Criterion
- Artikel/kapitelEngelska2019
Förlag, utgivningsår, omfång ...
-
2019-07-29
-
MDPI,2019
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:kth-261040
-
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-261040URI
-
https://doi.org/10.3390/polym11081251DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
QC 20191002
-
Determining a suitable and reliable end-of-lifetime criterion for O-ring seals is an important issue for long-term seal applications. Therefore, seal failure of ethylene propylene diene rubber (EPDM) and hydrogenated nitrile butadiene rubber (HNBR) O-rings aged in the compressed state at 125 degrees C and at 150 degrees C for up to 1.5 years was analyzed and investigated under static conditions, using both non-lubricated and lubricated seals. Changes of the material properties were analyzed with dynamic-mechanical analysis and permeability experiments. Indenter modulus measurements were used to investigate DLO effects. It became clear that O-rings can remain leak-tight under static conditions even when material properties have already degraded considerably, especially when adhesion effects are encountered. As a feasible and reliable end-of-lifetime criterion for O-ring seals under static conditions should include a safety margin for slight dimensional changes, a modified leakage test involving a small and rapid partial decompression of the seal was introduced that enabled determining a more realistic but still conservative end-of-lifetime criterion for an EPDM seal.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Jaunich, MatthiasBundesanstalt Mat Forsch & Prufung, D-12200 Berlin, Germany.
(författare)
-
Pourmand, PayamKTH,Fiber- och polymerteknologi(Swepub:kth)u1v951wj
(författare)
-
Wolff, DietmarBundesanstalt Mat Forsch & Prufung, D-12200 Berlin, Germany.
(författare)
-
Hedenqvist, Mikael S.KTH,Fiber- och polymerteknologi(Swepub:kth)u10rkaxe
(författare)
-
Bundesanstalt Mat Forsch & Prufung, D-12200 Berlin, Germany.Fiber- och polymerteknologi
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Polymers: MDPI11:82073-4360
Internetlänk
Hitta via bibliotek
-
Polymers
(Sök värdpublikationen i LIBRIS)
Till lärosätets databas