Nanocrystallinity in RuO2 coatings-Influence of precursor and preparation temperature
-
- Malmgren, Christine (författare)
- Mittuniversitetet,Institutionen för naturvetenskap, teknik och matematik (-2012),Mid Sweden University
-
- Eriksson, Annika, 1975 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Cornell, Ann (författare)
- KTH,Tillämpad elektrokemi,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)
-
visa fler...
-
- Bäckström, Joakim (författare)
- Mittuniversitetet,Institutionen för naturvetenskap, teknik och matematik (-2012),Mid Sweden University
-
- Eriksson, Sten, 1958 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Olin, Håkan (författare)
- Mittuniversitetet,Institutionen för naturvetenskap, teknik och matematik (-2012),Mid Sweden University
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2010
- 2010
- Engelska.
-
Ingår i: Thin Solid Films. - : Elsevier BV. - 0040-6090 .- 1879-2731. ; 518:14, s. 3615-3618
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- The effects of precursor and calcination temperature on the nano morphology of ruthenium dioxide on titanium, prepared from thermal decomposition of aqueous salt solutions were investigated. Transmission electron microscopy. X-ray diffraction, gas porosimetry and cyclic voltammetry showed that lower calcination temperature yielded smaller crystallites. The crystallites were between 6 and 22 nm in diameter. When using ruthenium nitrosyl nitrate the firing temperature had a large impact on the grain size, but for chloride there was only a minor effect in the temperature range 350-550 degrees C.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Nyckelord
- Ruthenium nitrosyl nitrate
- Crystallization
- X-ray diffraction
- Catalysis
- Annealing
- Chemical engineering
- Kemiteknik
- Materials science
- Teknisk materialvetenskap
- NATURAL SCIENCES
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas