Delayed Hydride Cracking in Irradiated Zircaloy Cladding

Efsing, Pål, 1965- (författare)
KTH,Skolan för teknikvetenskap (SCI)
Pettersson, Kjell (författare)
KTH,Mekanisk metallografi,Tidigare Institutioner (före 2005)
 (creator_code:org_t)
STP1354
USA : ASTM International, 2000
2000
Engelska.
Ingår i: <em>Zirconium in the Nuclear Industry: Twelfth International Symposium</em>. - USA : ASTM International. ; , s. 340-355
  • Bokkapitel (refereegranskat)
Abstract Ämnesord
Stäng  
  • Slow stable crack growth by a mechanism identified as a form of delayed hydride cracking has been studied on irradiated Zircaloy cladding. The background to the investigation was the formation of long axial cracks in defected fuel rods. Post-irradiation examination of such fuel rods has indicated that precipitation and subsequent cracking of hydrides at the tips of the long cracks has played an important role in the crack growth process. The present investigation conducted on irradiated cladding with hydrogen concentrations above about 500 ppm has demonstrated that a hydrogen-induced crack growth process can occur in such material. In the laboratory it was necessary to subject the samples to an overtemperature cycle in order to initiate crack growth after fatigue precracking. It was also observed that an incubation time on the order of 20 h was necessary before crack growth started. The crack growth rates were strongly dependent on the applied stress intensity factor K in a narrow range above a threshold value KIH, which was about 10 MPa√m, Stage I. The growth rate then reached a plateau value when it was independent of K, Stage II. This plateau value was about 10-6 m/s at 300°C and about 2 × 10-7 m/s at 200°C. This temperature dependence is consistent with a mechanism based on stress-induced diffusion of hydrogen at the stress concentration of the crack tip. Metallographic and fractographic observations suggest that the details of the mechanism can be best described as a localized reduction of fracture toughness due to reorientation of hydrides so that they become perpendicular to the applied stress in the region of the crack tip. This is somewhat in contrast to previous DHC mechanisms in which longer-range diffusion of hydrogen to one large hydride at the crack tip is usually modeled. The difference is that in the present case the hydride content is higher and therefore more hydrides are present.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)
TEKNIK OCH TEKNOLOGIER  -- Maskinteknik -- Teknisk mekanik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering -- Applied Mechanics (hsv//eng)

Nyckelord

Zircaloy
delayed hydride cracking
crack growth
hydrides
irradiation effects
threshold stress intensity
Kärnenergiteknik
Nuclear Engineering
Hållfasthetslära

Publikations- och innehållstyp

ref (ämneskategori)
kap (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Hitta mer i SwePub

Av författaren/redakt...
Efsing, Pål, 196 ...
Pettersson, Kjel ...
Om ämnet
TEKNIK OCH TEKNOLOGIER
TEKNIK OCH TEKNO ...
och Materialteknik
och Annan materialte ...
TEKNIK OCH TEKNOLOGIER
TEKNIK OCH TEKNO ...
och Maskinteknik
och Teknisk mekanik
Artiklar i publikationen
Av lärosätet
Kungliga Tekniska Högskolan

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy