Relating stress/strain heterogeneity to lath martensite strength by experiments and dislocation density-based crystal plasticity

Artikel/kapitelEngelska2024

Förlag, utgivningsår, omfång ...

Elsevier BV,2024
printrdacarrier

Nummerbeteckningar

LIBRIS-ID:oai:DiVA.org:kth-344969
https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-344969URI
https://doi.org/10.1016/j.ijplas.2024.103917DOI

Kompletterande språkuppgifter

Språk:engelska
Sammanfattning på:engelska

Ingår i deldatabas

SwePubSwePub

Klassifikation

Ämneskategori:ref swepub-contenttype
Ämneskategori:art swepub-publicationtype

Anmärkningar

QC 20240404
To enhance the fundamental understanding for micromechanical lath martensite deformation, the microstructure as well as macro- and microscopic tensile properties of as -quenched 15-5 PH stainless steel are systematically analysed depending on the austenitisation temperature. Based on electron backscatter diffraction (EBSD) and backscattered electron (BSE) analysis, it is noted that the martensite morphology alters from a less defined to a more clearly defined parallel arrangement of the block and lath structure with increasing temperature. For an indepth quantification of the hierarchical boundary strengthening contributions in relation to local stress/strain heterogeneity, separate high-fidelity virtual microstructures are realised for the different scales (prior austenite grains, packets and blocks). This is consistent with the materials transformation process. The virtual microstructures are simulated employing the crystal plasticity finite element method (CPFEM) adapted for handling high dislocation density and encompassing all relevant strengthening mechanisms by boundaries, dislocations and solute atoms. While accurately capturing the measured size -dependent stress-strain behaviour, the simulations reveal in line with the experiments (Hall-Petch) that blocks are the most effective dislocation motion barrier, causing increased strain hardening and stress/strain heterogeneity. Furthermore, since strain localisation is predicted strongest in the distinct block structure, the experimentally observed early plastic material yielding is thought to be favoured here.

Ämnesord och genrebeteckningar

TEKNIK OCH TEKNOLOGIER Materialteknik Annan materialteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Other Materials Engineering hsv//eng
Martensite
Microstructure
EBSD
Mechanical properties
Modelling

Biuppslag (personer, institutioner, konferenser, titlar ...)

Zhou, TaoKTH,Strukturer(Swepub:kth)u1mni15g (författare)
Dahlberg, Carl F. O.,1980-KTH,Hållfasthetslära(Swepub:kth)u11tguno (författare)
Hedström, PeterKTH,Egenskaper(Swepub:kth)u1hu0w18 (författare)
KTHEgenskaper (creator_code:org_t)

Sammanhörande titlar

Ingår i:International journal of plasticity: Elsevier BV1740749-64191879-2154

Internetlänk

Hitta via bibliotek

International journal of plasticity (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

1 av 1
Föregående post
Nästa post
Till träfflistan

Hitta mer i SwePub

Av författaren/redakt...: Fischer, Tim; Zhou, Tao; Dahlberg, Carl F ...; Hedström, Peter

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Annan materialte ...

Artiklar i publikationen: International jo ...

Av lärosätet: Kungliga Tekniska Högskolan

Sök utanför SwePub

Sök vidare i:: Google; Google Book Search; Google Scholar

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

LIBRIS.kb.se