Comparative study of 4H-SiC irradiated with neutrons and heavy ions

• The influence of the irradiation with neutrons, Kr+ (245 MeV) and Bi+ (710 MeV) ions on the optical and electrical properties of high-resistivity, high-purity 4H-SiC epitaxial layers grown by chemical vapor deposition was investigated using photoluminescence and deep-level transient spectroscopy. Electrical characteristics were studied using Al and Cr Schottky barriers as well as p(+)-n-n(+) diodes fabricated by Al ion implantation on this epitaxial layers. It was found that both "light" neutrons and high energy heavy ions introduced identical defect centers in 4H-SiC. So, even at extremely high density of the ionization energy of 34 keV/mn, typical for Bi+ ion bombardment, damage structure formation in SiC single crystal is governed by energy loss in elastic collisions.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

Nyckelord

SiC

irradiation

neutrons

bismuth

krypton

luminescence

defects

deep level

Publikations- och innehållstyp

ref (ämneskategori)

kon (ämneskategori)