Influence of B2O3 on Viscosity of High Ti-bearing Blast Furnace Slag
-
- Ren, Shan (författare)
- Univ Sci & Technol Beijing, Peoples R China
-
- Zhang, Jianliang (författare)
- Univ Sci & Technol Beijing, Peoples R China
-
- Wu, Liushun (författare)
- KTH,Mikro-modellering
-
visa fler...
-
- Liu, Weijian (författare)
- Univ Sci & Technol Beijing, Peoples R China
-
- Bai, Yanan (författare)
- Univ Sci & Technol Beijing, Peoples R China
-
- Xing, Xiangdong (författare)
- Univ Sci & Technol Beijing, Peoples R China
-
- Su, Buxin (författare)
- Univ Sci & Technol Beijing, Peoples R China
-
- Kong, Dewen (författare)
- Univ Sci & Technol Beijing, Peoples R China
-
visa färre...
-
(creator_code:org_t)
- Iron and Steel Institute of Japan, 2012
- 2012
- Engelska.
-
Ingår i: ISIJ International. - : Iron and Steel Institute of Japan. - 0915-1559 .- 1347-5460. ; 52:6, s. 984-991
- Relaterad länk:
-
https://www.jstage.j...
-
visa fler...
-
https://urn.kb.se/re...
-
https://doi.org/10.2...
-
visa färre...
Abstract
Ämnesord
Stäng
- The influence of B2O3 on the viscosity of high Ti-bearing BF slag is studied under Ar atmosphere from 1 773 K (1 500 degrees C) to about 1 593 K (1 320 degrees C). The results show that the addition of B2O3 can decrease the viscosity of high Ti-bearing BF Slag containing UPC, consequently improve its fluidity. With the existence of 1.5% UPC, when the content of B2O3 increased from 0 to 4.1%, the volume fraction of perovskite decreased from 7.7% to 1.6% at 1 610 K. Meanwhile, the liquidus temperatures decreased from 1 619 K to 1 613 K. At a lower temperature, B2O3 was easy to form a eutectic and decreased the viscosity of molten slag. At a higher temperature, some tetrahedron [BO4](5-) changed into triangle [BO3](3-) which would disintegrate the chains/molecules of molten matrix and decreased its viscosity.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- Ti-bearing blast furnace slag
- viscosity
- B2O3