Structure and properties of Cr–C/Ag films deposited by magnetron sputtering
- Artikel/kapitelEngelska2015
Förlag, utgivningsår, omfång ...
-
Elsevier,2015
-
electronicrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:liu-169093
-
https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-169093URI
-
https://doi.org/10.1016/j.surfcoat.2015.09.054DOI
-
https://urn.kb.se/resolve?urn=urn:nbn:se:liu:diva-123411URI
-
https://urn.kb.se/resolve?urn=urn:nbn:se:uu:diva-247276URI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Cr–C/Ag thin films with 0–14 at.% Ag have been deposited by magnetron sputtering from elemental targets. The samples were analyzed by X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) to study their structure and chemical bonding. A complex nanocomposite structure consisting of three phases; nanocrystalline Ag, amorphous CrCx and amorphous carbon is reported. The carbon content in the amorphous carbide phase was determined to be 32–33 at.% C, independent of Ag content. Furthermore, SEM and XPS results showed higher amounts of Ag on the surface compared to the bulk. The hardness and Young's modulus were reduced from 12 to 8 GPa and from 270 to 170 GPa, respectively, with increasing Ag content. The contact resistance was found to decrease with Ag addition, with the most Ag rich sample approaching the values of an Ag reference sample. Initial tribological tests gave friction coefficients in the range of 0.3 to 0.5, with no clear trends. Annealing tests show that the material is stable after annealing at 500 °C for 1 h, but not after annealing at 800 °C for 1 h. In combination, these results suggest that sputtered Cr–C/Ag films could be potentially applicable for electric contact applications.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Nygren, KristianUppsala universitet,Oorganisk kemi,Uppsala University, Uppsala, Sweden; Impact Coatings AB, Linköping, Sweden(Swepub:uu)kriny267
(författare)
-
Malinovskis, PauliusUppsala universitet,Oorganisk kemi,Uppsala University, Uppsala, Sweden(Swepub:uu)pauma842
(författare)
-
Palisaitis, Justinas,1983-Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten,Tekniska högskolan(Swepub:liu)juspa01
(författare)
-
Persson, Per O. Å.,1971-Linköpings universitet,Tunnfilmsfysik,Tekniska fakulteten(Swepub:liu)perpe25
(författare)
-
Lewin, Erik,1979-Uppsala universitet,Oorganisk kemi,Uppsala University, Uppsala, Sweden(Swepub:uu)leeri169
(författare)
-
Jansson, UlfUppsala universitet,Oorganisk kemi,Uppsala University, Uppsala, Sweden(Swepub:uu)uja03434
(författare)
-
Uppsala universitetOorganisk kemi
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Surface & Coatings Technology: Elsevier281, s. 184-1920257-89721879-3347
Internetlänk
Hitta via bibliotek
Till lärosätets databas