Early stage spinodal decomposition and microstructure evolution in TiAlN : A combined in-situ SAXS and phase field study
-
- Knutsson, Axel (författare)
- Linköpings universitet,Nanostrukturerade material,Tekniska högskolan
-
- Ullbrand, Jennifer (författare)
- Linköpings universitet,Nanostrukturerade material,Tekniska högskolan
-
- Rogström, Lina (författare)
- Linköpings universitet,Nanostrukturerade material,Tekniska högskolan
-
visa fler...
-
- Norrby, Niklas (författare)
- Linköpings universitet,Nanostrukturerade material,Tekniska högskolan
-
- Hultman, Lars (författare)
- Linköpings universitet,Tunnfilmsfysik,Tekniska högskolan
-
- Almer, Jonathan (författare)
- Argonne National Laboratory, Illinois, USA,Advanced Photon Source
-
- Johansson, Mats P. (författare)
- Linköpings universitet,Nanostrukturerade material,Tekniska högskolan
-
- Jansson, Bo (författare)
- Seco Tools AB, Fagersta, Sweden
-
- Magnus, Odén (författare)
- Linköpings universitet,Nanostrukturerade material,Tekniska högskolan,Nanostructured Materials
-
visa färre...
-
(creator_code:org_t)
- Engelska.
- Relaterad länk:
-
https://urn.kb.se/re...
Abstract
Ämnesord
Stäng
- This paper describes in detail the microstructure and phase evolution in Ti0.33Al0.67N and Ti0.50Al0.50N coatings during isothermal annealing, studied by in-situ small angle x-ray scattering (SAXS), in combination with phase field simulations. We show that the isostructural spinodal decomposition occurs in two stages. During the initial stage, the phase segregation proceeds with a constant size of AlN- and TiN-rich domains with an experimentally measured radius of ~0.7 nm for 5 and 20 min at 900 and 850 °C respectively in the Ti0.50Al0.50N alloy. The length of the initial stage depends on temperature as well as metal composition, and is shorter for the higher Al-content coating. After the initial stage, the coherent cubic AlN- and TiN-rich domains coarsen. The coarsening process is kinetically limited by diffusion, which allowed us to estimate the diffusivity and activation energies of the metals to 1.4·10-7 m2s-1 and 3.14 eV at-1 respectively.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Keramteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Ceramics (hsv//eng)
Nyckelord
- TiAlN
- Phase-field simulations
- Spinodal decomposition
- SAXS
- High energy x-ray diffraction
- Coarsening
Publikations- och innehållstyp
- vet (ämneskategori)
- ovr (ämneskategori)