The effect of single-side ion exchange on the flexural strength of plain and holed float glass containing a drilled hole
-
- Karlsson, Stefan, 1984- (författare)
- Linnéuniversitetet,Institutionen för bygg- och energiteknik (BE),Glass Group
-
- Jonson, Bo (författare)
- Linnéuniversitetet,Institutionen för bygg- och energiteknik (BE),Glass Group
-
- Johansson, Marie (författare)
- Linnéuniversitetet,Institutionen för bygg- och energiteknik (BE)
-
visa fler...
-
- Enquist, Bertil (författare)
- Linnéuniversitetet,Institutionen för bygg- och energiteknik (BE)
-
visa färre...
-
(creator_code:org_t)
- 2013
- 2013
- Engelska.
-
Ingår i: European Journal of Glass Science and Technology. Part A: Glass Technology. - 1753-3546. ; 54:2, s. 66-71
- Relaterad länk:
-
http://www.ingentaco...
-
visa fler...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- The effect of single-side ion exchange (using a KNO3:KCl mixture) on the ring-on-ring flexural strength of float glass has been studied. Two ion exchanged series, treated at 450 and 515°C, were investigated. The ion exchanged samples showed approximately 160 respectively 100% increases in their arithmetic mean strength compared to as-received float glass. Furthermore, a series of samples containing drilled holes were studied in order to investigate the effect of single-side ion exchange on such common construction elements. The samples that contained drilled holes were ion exchanged at 450°C and showed around 140% increase of the fracture load compared to the untreated samples containing drilled holes. As a general observation, the ion exchange treatment induced ~110 MPa compressive stresses (515°C) and ~180 MPa compressive stresses (450°C). The ion exchanged samples showed no significant increase in stiffness.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
Nyckelord
- Float glass
- Ion exchange
- Flexural strength
- Coaxial double ring-test
- Glasteknologi
- Glass Technology
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas