Tensile strength of handsheets prepared with macerated fibres from solid wood modified with cross-linking agents
- Artikel/kapitelEngelska2015
Förlag, utgivningsår, omfång ...
- 2014-12-17
- Walter de Gruyter,2015
- printrdacarrier
Nummerbeteckningar
- LIBRIS-ID:oai:DiVA.org:lnu-41786
- https://urn.kb.se/resolve?urn=urn:nbn:se:lnu:diva-41786URI
- https://doi.org/10.1515/hf-2014-0216DOI
Kompletterande språkuppgifter
- Språk:engelska
- Sammanfattning på:engelska
Ingår i deldatabas
- SwePubSwePub
Klassifikation
Anmärkningar
- This study was conducted to explain the tensile strength loss of wood due to the modification with 1,3-dimethylol-4,5-dihydroxyethyleneurea (DMDHEU) and glutaraldehyde (GA). Modified and control wood blocks were macerated to deliberate fibres, and handsheets were produced thereof. The nitrogen content of the fibres indicated that maceration removed the major proportions of DMDHEU. The stability of GA in wood during maceration was not assessed. Tensile strength determined at zero span (z-strength) and finite span (f-strength) was equal for the handsheets from DMDHEU-modified fibres and the control handsheets. The microscopic appearance of the tested finite-span paper strips from DMDHEU-modified fibres mainly indicated interfibre failure and did not differ from the fibre fracture mode of the control handsheets. In contrast, the z-strength of the handsheets from GA-modified fibres was lower than that of controls and decreased with increasing content of GA in the initial modified wood. The f-strength behaviour of the handsheets from GA-modified fibres was the opposite: it was higher than that of controls and increased with increasing GA content. The microscopic appearance of the rapture zones of the finite-span testing mainly indicated intrafibre failure for the GA-modified fibres. It was concluded that cross-linking is likely to be the major reason for tensile strength loss of GA- and DMDHEU-modified wood. In terms of DMDHEU-modified wood, the incrustation of the cell wall by the resin and the reduction in pliability could play an additional role.
Ämnesord och genrebeteckningar
- LANTBRUKSVETENSKAPER Lantbruksvetenskap, skogsbruk och fiske Trävetenskap hsv//swe
- AGRICULTURAL SCIENCES Agriculture, Forestry and Fisheries Wood Science hsv//eng
- brittleness
- cross-linking
- DMDHEU
- finite span
- glutaraldehyde
- tensile strength
- wood modification
- zero span
- Forestry and Wood Technology
- Skog och träteknik
Biuppslag (personer, institutioner, konferenser, titlar ...)
- Hosseinpourpia, RezaGeorg-August-University Göttingen, Germany,GoFP(Swepub:lnu)rehoaa (författare)
- Mai, CarstenGeorg-August-University Göttingen, Germany (författare)
- Technological Educational Institute of Thessaly, GreeceGoFP (creator_code:org_t)
Sammanhörande titlar
- Ingår i:Holzforschung: Walter de Gruyter69:8, s. 959-9660018-38301437-434X
Internetlänk
- 1 av 1
- Föregående post
- Nästa post
- Till träfflistan
Hitta mer i SwePub
- Av författaren/redakt...
- Adamopoulos, Ste ...
- Hosseinpourpia, ...
- Mai, Carsten
- Om ämnet
-
- LANTBRUKSVETENSKAPER
- LANTBRUKSVETENSK ...
- och Lantbruksvetensk ...
- och Trävetenskap
- Artiklar i publikationen
- Holzforschung
- Av lärosätet
- Linnéuniversitetet
Sök utanför SwePub
- Sök vidare i:
- Google Book Search
- Google Scholar
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.
- Copyright © LIBRIS - Nationella bibliotekssystem
- LIBRIS.kb.se