Melk, LatifaLuleå tekniska universitet,Materialvetenskap
(författare)
Coefficient of friction and wear resistance of zirconia-MWCNTs composites
- Artikel/kapitelEngelska2015
Förlag, utgivningsår, omfång ...
-
Elsevier BV,2015
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:ltu-2685
-
https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-2685URI
-
https://doi.org/10.1016/j.ceramint.2014.08.092DOI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Validerad; 2014; Nivå 2; 20140910 (andbra)
-
Composites of 3 mol.% yttria-doped tetragonal zirconia (3Y-TZP) reinforced with multiwalled carbon nanotubes (MWCNT) up to 2 wt. % content have been produced using spark plasma sintering (SPS). The theoretical densities of the studied composites were found to be between 99.4 and 97.4%. The addition of MWCNT content resulted in reduction of 3Y-TZP grain size from 174 to 148 nm. The effect of MWCNT on the friction coefficient (COF) was studied by performing nano- and macro-scratches using diamond Berkovich and Rockwell indenters, respectively. Moreover, the COF and the wear rate were also investigated in reciprocating sliding against a zirconia ball under a load of 5 N. The results showed that the COF decreased upon the increase in MWCNT content. However, in macro-scratch testing, there was a critical load over which brittle fracture sets in and its value decreases as the MWCNT content increases. The wear resistance was found to be decreasing very slightly for less than 1 wt. % MWCNT, while it increases strongly for the addition of 2 wt. % MWCNT under the conditions studied. The results were discussed in terms of material properties, scanning electron microscopy observations of the wear track and nanoindentation tests.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Rovira, Joan Josep RoaDepartment of Materials Science and Engineering, Universitat Politècnica de Catalunya, Barcelona
(författare)
-
Antti, Marta-LenaLuleå tekniska universitet,Materialvetenskap(Swepub:ltu)marta
(författare)
-
Anglada, MarcDepartment of Materials Science and Engineering, Universitat Politècnica de Catalunya, Barcelona
(författare)
-
Luleå tekniska universitetMaterialvetenskap
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Ceramics International: Elsevier BV41:1 Part A, s. 459-4680272-88421873-3956
Internetlänk
Hitta via bibliotek
Till lärosätets databas