Adhesion tendency of PVD TiAlN coatings at elevated temperatures during reciprocating sliding against carbon steel
-
- Courbon, Cedric (författare)
- Luleå tekniska universitet,Maskinelement
-
- Fallqvust, M. (författare)
- R&D Materials and Technology Development, Seco Tools AB, Fagersta
-
- Hardell, Jens (författare)
- Luleå tekniska universitet,Maskinelement
-
visa fler...
-
- M'Saoubi, R. (författare)
- R&D Materials and Technology Development, Seco Tools AB, Fagersta
-
- Prakash, Braham (författare)
- Luleå tekniska universitet,Maskinelement
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2015
- 2015
- Engelska.
-
Ingår i: Wear. - : Elsevier BV. - 0043-1648 .- 1873-2577. ; 330-331, s. 209-222
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- This work focussed on assessing the contact conditions driving the adhesion tendency of PVD TiAlN coated cemented carbide during reciprocating sliding against a normalized AISI 4137 carbon steel. A special emphasis is given to the surface topography of the coating. Results are analysed in terms of friction and material transfer over a large range of temperatures (up to 800 °C) and contact pressures. The post-test surface analysis of the specimens is conducted in order to understand the tribological behaviour and elucidate the formation mechanisms of transfer layers. A numerical model is developed to assess the amount of heat effectively transmitted into the first bodies and the temperature of the surfaces in contact.Whereas temperatures close to 400 °C ensure the formation of a stable tribofilm reducing friction, the highest temperatures lead to unstable frictional behaviour. Coating surface topography has been seen to be a major parameter driving material transfer during the first stages of the contact and the formation of a transfer layer. Thin and homogeneous layers are almost instantaneously formed with a polished surface whereas some time is required with a rougher one to form a film. A large amount of the frictional power is dissipated into these layers and high temperatures can be reached at the surface due to frictional heating. Contact pressure is found to be a parameter promoting transfer and oxidation
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Tribologi (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Tribology (hsv//eng)
Nyckelord
- Machine Elements
- Maskinelement
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
-
Wear
(Sök värdpublikationen i LIBRIS)
Till lärosätets databas