Mode II crack paths under compression in brittle solids: A theory and experimental comparison

↓ Direkt till sidans innehåll
↓ Direkt till sidans sekundära innehåll (sidomenyn)

Sökning: onr:"swepub:oai:DiVA.org:miun-1121" > Mode II crack paths...

1 av 1
Föregående post
Nästa post
Till träfflistan

Isaksson, PerMittuniversitetet,Institutionen för teknik, fysik och matematik (-2008),FSCN – Fibre Science and Communication Network (författare)

Mode II crack paths under compression in brittle solids : A theory and experimental comparison

Artikel/kapitelEngelska2002

Förlag, utgivningsår, omfång ...

2002
printrdacarrier

Nummerbeteckningar

LIBRIS-ID:oai:DiVA.org:miun-1121
https://urn.kb.se/resolve?urn=urn:nbn:se:miun:diva-1121URI
https://doi.org/10.1016/S0020-7683(02)00089-6DOI
https://urn.kb.se/resolve?urn=urn:nbn:se:mau:diva-2632URI

Kompletterande språkuppgifter

Språk:engelska
Sammanfattning på:engelska

Ingår i deldatabas

SwePubSwePub

Klassifikation

Ämneskategori:ref swepub-contenttype
Ämneskategori:art swepub-publicationtype

Anmärkningar

A study of crack propagation paths in the situation where the crack is suppressed to open during growth due to high compressive forces has been performed. This problem was analyzed theoretically very recently by the authors and is here extended to involve a limited number of illustrative experimental results reported elsewhere in the literature. By analyzing the experimental crack growth patterns, the conclusion is that the model cannot describe the more realistic microscopic failure in detail. Since shear crack growth on the microscale strongly depend on inhomogenities in the material, like cavities, grains or inclusions; the closed crack growth patterns observed are not smooth or free of kinks. Nevertheless, the model show good agreement with the reported experimental observations of the paths of closed macroscopic mode II cracks on samples in brittle materials, induced under overall compression. Failure patterns experimentally observed supports the theory that the growth of mode II cracks under compression in brittle materials follow a propagation path described by a function y ¼ kxb, where b ¼ 3=2. This is strongly supported by the measured values obtained from various experiments. In all the studied experiments, the exponent b was found in the interval [1.43–1.58]. Further, an investigation of the curvature parameter k has been performed and the conclusion is that k does also agree with the simplified model, even though not as good as the exponent b. However, k differs in general <15% from the theoretical value predicted by the model. The process of crack growth is in the simplified model assumed to be controlled by the mode II stress intensity factor KII of the main crack and the difference between the compressive remote normal stress parallel with the crack plane (r111) and the compressive remote normal stress perpendicular to the crack plane (r122).

Ämnesord och genrebeteckningar

TEKNIK OCH TEKNOLOGIER Materialteknik Pappers-, massa- och fiberteknik hsv//swe
ENGINEERING AND TECHNOLOGY Materials Engineering Paper, Pulp and Fiber Technology hsv//eng
TEKNIK OCH TEKNOLOGIER Maskinteknik Teknisk mekanik hsv//swe
ENGINEERING AND TECHNOLOGY Mechanical Engineering Applied Mechanics hsv//eng
Fracture mechanics
Cellulose and paper engineering
Cellulosa- och pappersteknik

Biuppslag (personer, institutioner, konferenser, titlar ...)

Ståhle, PerMalmö högskola,Teknik och samhälle (TS)(Swepub:mau)tspest (författare)
MittuniversitetetInstitutionen för teknik, fysik och matematik (-2008) (creator_code:org_t)

Sammanhörande titlar

Ingår i:International Journal of Solids and Structures39:8, s. 2281-22970020-76831879-2146

Internetlänk

Hitta via bibliotek

International Journal of Solids and Structures (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

1 av 1
Föregående post
Nästa post
Till träfflistan

Hitta mer i SwePub

Av författaren/redakt...: Isaksson, Per; Ståhle, Per

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Pappers massa oc ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Maskinteknik; och Teknisk mekanik

Artiklar i publikationen: International Jo ...

Av lärosätet: Mittuniversitetet; Malmö universitet

Sök utanför SwePub

Sök vidare i:: Google; Google Book Search; Google Scholar

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

LIBRIS.kb.se