The effect of single-side ion exchange on the flexural strength of plain float glass and float glass containing a drilled hole

Karlsson, Stefan,1984-RISE,Glafo Glasforskningsinstitutet,Linnaeus University, Sweden (författare)

The effect of single-side ion exchange (using a KNO3:KCl mixture) on the ring-on-ring flexural strength of float glass has been studied. Two ion exchanged series, treated at 450 and 515°C, were investigated. The ion exchanged samples showed approximately 160 respectively 100% increases in their arithmetic mean strength compared to as-received float glass. Furthermore, a series of samples containing drilled holes were studied in order to investigate the effect of singleside ion exchange on such common construction elements. The samples that contained drilled holes were ion exchanged at 450°C and showed around 140% increase of the fracture load compared to the untreated samples containing drilled holes. As a general observation, the ion exchange treatment induced ∼110 MPa compressive stresses (515°C) and ∼180 MPa compressive stresses (450°C). The ion exchanged samples showed no significant increase in stiffness.

Av författaren/redakt...: Karlsson, Stefan ...; Jonson, Bo; Johansson, Marie; Enquist, Bertil

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.