Oxygen reduction reaction and proton exchange membrane fuel cell performance of pulse electrodeposited Pt–Ni and Pt–Ni–Mo(O) nanoparticles
- Artikel/kapitelEngelska2022
Förlag, utgivningsår, omfång ...
-
Elsevier Ltd,2022
-
printrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:DiVA.org:ri-59325
-
https://urn.kb.se/resolve?urn=urn:nbn:se:ri:diva-59325URI
-
https://doi.org/10.1016/j.mtener.2022.101023DOI
-
https://urn.kb.se/resolve?urn=urn:nbn:se:hj:diva-56908URI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:ref swepub-contenttype
-
Ämneskategori:art swepub-publicationtype
Anmärkningar
-
Funding details: H2020 Marie Skłodowska-Curie Actions, MSCA, 764977; Funding details: Generalitat de Catalunya, 2017-SGR-292, PID2020-116844RB-C21; Funding details: Horizon 2020; Funding text 1: This work has received funding from the European Union's Horizon 2020 research and innovation programme under the Marie Skłodowska-Curie grant agreement No 764977, the Generalitat de Catalunya under project 2017-SGR-292, and the Spanish government under project PID2020-116844RB-C21. The authors want to express their thanks to Freudenberg, Germany, who gladly supported the GDL material for this study.
-
Proton exchange membrane fuel cells (PEMFCs) are an important alternative to fossil fuels and a complement to batteries for the electrification of vehicles. However, their high cost obstructs commercialization, and the catalyst material, including its synthesis, constitutes one of the major cost components. In this work, Pt–Ni and Pt–Ni–Mo(O) nanoparticles (NPs) of varying composition have been synthesized in a single step by pulse electrodeposition onto a PEMFC's gas diffusion layer. The proposed synthesis route combines NP synthesis and their fixation onto the microporous carbon layer in a single step. Both Pt–Ni and Pt–Ni–Mo(O) catalysts exhibit extremely high mass activities at oxygen reduction reaction (ORR) with very low Pt loadings of around 4 μg/cm2 due to the favorable distribution of NPs in contact with the proton exchange membrane. Particle sizes of 40–50 nm and 40–80 nm were obtained for Pt–Ni and Pt–Ni–Mo(O) systems, respectively. The highest ORR mass activities were found for Pt67Ni33 and Pt66Ni32–MoOx NPs. The feasibility of a single-step electrodeposition of Pt–Ni–Mo(O) NPs was successfully demonstrated; however, the ternary NPs are of more amorphous nature in contrast to the crystalline, binary Pt–Ni particles, due to the oxidized state of Mo. Nevertheless, despite their heterogeneous nature, the ternary NPs show homogeneous behavior even on a microscopic scale. © 2022 The Author(s)
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Mölmen, LiveRISE,Elektrifiering och pålitlighet,Jönköping University, Sweden,JTH, Material och tillverkning,Department of Electrification and Reliability, RISE Research Institutes of Sweden, Borås, Sweden(Swepub:hj)molliv
(författare)
-
Fast, LarsRISE,Elektrifiering och pålitlighet,Department of Electrification and Reliability, RISE Research Institutes of Sweden, Borås, Sweden(Swepub:ri)LarsF@ri.se
(författare)
-
Leisner, PeterJönköping University,JTH, Material och tillverkning(Swepub:hj)lepe
(författare)
-
Sort, JordiUniversitat Autònoma de Barcelona, Spain; ICREA, Spain,Department de Física, Universitat Autònoma de Barcelona, Bellaterra, 08193, Spain
(författare)
-
Pellicer, EvaDepartment de Física, Universitat Autònoma de Barcelona, Bellaterra, 08193, Spain
(författare)
-
Department de Física, Universitat Autònoma de Barcelona, Bellaterra, 08193, SpainElektrifiering och pålitlighet
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Materials Today Energy: Elsevier Ltd272468-6069
Internetlänk
Hitta via bibliotek
Till lärosätets databas