Photoluminescence properties of high-pressure-polymerized C60 nanorods in the orthorhombic and tetragonal phases.

Agnieszka Iwasiewicz-Wabnig
C60nanorods in two polymeric phases have been synthesized under differenthigh pressure and high temperature conditions. Orthorhombic and tetragonal phaseshave been identified from Raman spectra. The rod shape canbe kept under quasihydrostatic pressure. The photoluminescence intensity of thepolymeric C60 nanorods has been greatly enhanced compared with thatof pristine C60 nanorods. The main fluorescence band shifted from730 nm in the unpolymeric phase to 748 nm and near infrared780 nm in the orthorhombic and tetragonal phases, respectively. The enhancedphotoluminescence with tunable frequency for different polymeric C60 nanorods suggestspotential applications in luminescent nanomaterials.

Liu, Bingbing (författare)
Wang, Lin (författare)
Yu, Shidan (författare)
Yao, Mingguang (författare)
Chen, Ao (författare)
Liu, Dedi (författare)
Cui, Tian (författare)
Zou, Guangtian (författare)
Iwasiewicz, AgnieszkaUmeå universitet,Institutionen för fysik(Swepub:umu)agaiwz02 (författare)
Sundqvist, BertilUmeå universitet,Institutionen för fysik(Swepub:umu)besu0001 (författare)
Umeå universitetInstitutionen för fysik (creator_code:org_t)

Ingår i:Applied Physics Letters: AIP Publishing89:18, s. 181925-0003-69511077-3118

Av författaren/redakt...: Hou, Yuanyuan; Liu, Bingbing; Wang, Lin; Yu, Shidan; Yao, Mingguang; Chen, Ao; visa fler...; Liu, Dedi; Cui, Tian; Zou, Guangtian; Iwasiewicz, Agni ...; Sundqvist, Berti ...; visa färre...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.