Fe/V and Fe/Co(001) superlattices: growth, anisotropy, magnetisation and magnetoresistance

Nordblad, PerUppsala universitet,Institutionen för teknikvetenskaper,Teoretisk magnetism,Fasta tillståndets fysik (författare)

Some physical properties of BCC Fe/V and Fe/Co (0 0 1) superlattices are reviewed. The dependence of the magnetic anisotropy on the in-plane strain introduced by the lattice mismatch between Fe and V is measured and compared to a theoretical derivation. The dependence of the magnetic anisotropy (and saturation magnetisation) on the layer thickness ratio Fe/Co is measured and a value for the anisotropy of BCC Co is derived from extrapolation. The interlayer exchange coupling of Fe/V superlattices is studied as a function of the V layer thickness (constant Fe thickness) and layer thickness of Fe (constant V thickness). A region of antiferromagnetic coupling and GMR is found for V thicknesses 12-14 monolayers. However, surprisingly, a 'cutoff' of the antiferromagnetic coupling and GMR is found when the iron layer thickness exceeds about 10 monolayers.

Broddefalk, A. (författare)
Mathieu, R. (författare)
Blomqvist, P. (författare)
Eriksson, OlleUppsala universitet,Teoretisk magnetism,Fasta tillståndets fysik(Swepub:uu)olleerik (författare)
Wappling, R. (författare)
Uppsala universitetInstitutionen för teknikvetenskaper (creator_code:org_t)

Av författaren/redakt...: Nordblad, Per; Broddefalk, A.; Mathieu, R.; Blomqvist, P.; Eriksson, Olle; Wappling, R.

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.