Synthesis of calcium phosphate crystals with thin nacreous structure

Nacre-like structures have attracted great interest in recent years due to their outstanding toughness, stiffness and impact resistance. However, there is a challenge associated with engineering nacre-like calcium phosphate crystals. In this study, thin nacreous-like monetite sheets were synthesized in solutions guided by a surfactant. The influence of temperature, initial pH, Ca/P ratio, stirring time and the concentration of cetyltrimethylammonium bromide (CTAB) on the nacre-like structure has been studied. Findings showed that a nacre-like structure could only be formed at a high temperature (90 degrees C), high initial pH (11), sufficient stirring time (3 h), and under the presence of CTAB. A small-angle X-ray scattering experiment carried out at a synchrotron radiation facility showed that the distance between nanolayers was around 2.6 nm and TEM confirmed the fine sheet-like structure. The mechanism of the formation the nacre-like structure and its characterization were discussed.

Grandfield, KathrynMcMaster University(Swepub:uu)katgr445 (författare)
Yu, ShunKTH (författare)
Engqvist, HåkanUppsala universitet,Tillämpad materialvetenskap(Swepub:uu)hakaengq (författare)
Xia, WeiUppsala universitet,Tillämpad materialvetenskap,Materials in Medcine(Swepub:uu)weixi400 (författare)
Uppsala universitetTillämpad materialvetenskap (creator_code:org_t)

Ingår i:CrystEngComm: Royal Society of Chemistry (RSC)18:6, s. 1064-10691466-8033

Av författaren/redakt...: Chen, Song; Grandfield, Kath ...; Yu, Shun; Engqvist, Håkan; Xia, Wei

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Industriell biot ...; och Biomaterial

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.