Theoretical shear strength and the onset of plasticity in nanodeformation of cubic boron nitride
-
- Dub, S. N. (författare)
- National Academy of Sciences of Ukraine
-
- Petrusha, I. A. (författare)
- National Academy of Sciences of Ukraine
-
- Bushlya, V. M. (författare)
- Lund University,Lunds universitet,Industriell Produktion,Institutionen för maskinvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Production and Materials Engineering,Department of Mechanical Engineering Sciences,Departments at LTH,Faculty of Engineering, LTH
-
visa fler...
-
- Taniguchi, T. (författare)
- National Institute for Materials Science, Tsukuba
-
- Belous, V. A. (författare)
- National Science Center Kharkov Institute of Physics and Technology
-
- Tolmachova, G. N. (författare)
- National Science Center Kharkov Institute of Physics and Technology
-
- Andreev, A. V. (författare)
- National Institute for Materials Science, Tsukuba
-
visa färre...
-
(creator_code:org_t)
- 2017
- 2017
- Engelska 11 s.
-
Ingår i: Journal of Superhard Materials. - 1063-4576. ; 39:2, s. 88-98
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://lup.lub.lu.s...
-
https://doi.org/10.3...
-
visa färre...
Abstract
Ämnesord
Stäng
- The nanoindentation in the continuous stiffness measurement mode was used to investigate the onset of plasticity at the nanodeformation of cubic boron nitride (cBN). This technique allows us to reveal an elastic-plastic transition in the contact and to measure the yield strength of cBN at the nanoscale. An abrupt elastoplastic transition (a pop-in) was observed in the (111) cBN single crystal as a result of a homogeneous or heterogeneous nucleation of dislocations in the previously dislocations-free region under the contact. The analysis of the data obtained at the homogeneous nucleation of dislocations in the contact region made it possible to experimentally estimate the theoretical shear strength of cBN and its ideal (elastic) hardness. In a sample of the fine-grained cBN with a nanotwinned substructure a smooth elastoplastic transition was observed in consequence of the propagation and multiplication of already existing dislocations in the contact region.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Keramteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Ceramics (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Teknisk mekanik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Applied Mechanics (hsv//eng)
Nyckelord
- cBN
- mechanical properties
- nanoindentation
- nucleation of dislocations
- theoretical shear strength