Characterization of White Layer Generated when Turning Aged Inconel 718
-
- Bushlya, Volodymyr (författare)
- Lund University,Lunds universitet,Industriell Produktion,Institutionen för maskinvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Production and Materials Engineering,Department of Mechanical Engineering Sciences,Departments at LTH,Faculty of Engineering, LTH
-
- Zhou, Jinming (författare)
- Lund University,Lunds universitet,Industriell Produktion,Institutionen för maskinvetenskaper,Institutioner vid LTH,Lunds Tekniska Högskola,Production and Materials Engineering,Department of Mechanical Engineering Sciences,Departments at LTH,Faculty of Engineering, LTH
-
- Lenrick, Filip (författare)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
- visa fler...
- Avdovic, Pajazit (författare)
- Brinksmeier, Ekkard (redaktör/utgivare)
- Jawahir, Ibrahim (redaktör/utgivare)
- visa färre...
- (creator_code:org_t)
- Elsevier BV, 2011
- 2011
- Engelska 7 s.
- Ingår i: Procedia Engineering. - : Elsevier BV. - 1877-7058. ; 19, s. 60-66
- Konferensbidrag (refereegranskat)
Abstract
Ämnesord
Stäng
- Abstract in UndeterminedWhite layer formation is considered as a part of minimum array of parameters characterizing surface integrity of the machined product. The paper is aimed on identification and characterization of white layer generated when finish turning aged Inconel 718 with Al2O3-SiCw ceramic tools under different cutting conditions, tool wear and coolant application. As expected intensity of white layer formation was proportional to cutting speed and tool wear. High resolution transmission electron microscopy (HRTEM) performed on white layer revealed formation of nanostructured material with grain size of 50-150 nm. Long-term ultrasonic-assisted etching of white layer allowed to uncover its morphology, where subsequent AFM measurements confirmed HRTEM findings. Observations by high resolution SEM provided evidence that gamma' Ni-3(Al,Ti) phase remained intact. (C) 2012 Published by Elsevier Ltd. Selection and peer-review under responsibility of Prof. E. Brinksmeier
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- Transmission electron microscopy
- Nickel alloy
- Surface integrity
- White layer
Publikations- och innehållstyp
- kon (ämneskategori)
- ref (ämneskategori)
- 1 av 1
- Föregående post
- Nästa post
- Till träfflistan
Hitta mer i SwePub
- Av författaren/redakt...
- Bushlya, Volodym ...
- Zhou, Jinming
- Lenrick, Filip
- Avdovic, Pajazit
- Ståhl, Jan-Eric
- Brinksmeier, Ekk ...
- visa fler...
- Jawahir, Ibrahim
- visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
- TEKNIK OCH TEKNO ...
- och Materialteknik
- Artiklar i publikationen
- Procedia Enginee ...
- Av lärosätet
- Lunds universitet
Sök utanför SwePub
- Sök vidare i:
- Google Book Search
- Google Scholar
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.
- Copyright © LIBRIS - Nationella bibliotekssystem
- LIBRIS.kb.se