Proton conduction in Perovskite Oxide BaZr0.5Yb0.5O3-δ Prepared by Wet Chemical Route
-
- Ahmed, Istaq, 1972 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Knee, Christopher, 1973 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för kemi,Department of Chemistry
-
- Eriksson, Sten, 1958 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
- Ahlberg, Elisabet, 1952 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för kemi,Department of Chemistry
-
- Karlsson, Maths, 1978 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Matic, Aleksandar, 1968 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Börjesson, Lars, 1957 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- The Electrochemical Society, 2008
- 2008
- Engelska.
-
Ingår i: Journal of the Electrochemical Society. - : The Electrochemical Society. - 1945-7111 .- 0013-4651. ; 155:11, s. 97-102
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://doi.org/10.1...
-
https://research.cha...
-
https://gup.ub.gu.se...
-
visa färre...
Abstract
Ämnesord
Stäng
- A wet chemical route has been used to synthesize the oxygen deficient perovskite Ba Zr0.5 Yb0.5 O3-δ. Analysis of X-ray powder diffraction data showed that both dried and hydrated samples adopt cubic crystal structures of space group Pm 3- m. Dynamic thermogravimetric analysis showed a significant mass loss for the hydrated sample compared to the dried sample, indicating that ∼28% of the oxygen vacancies are filled by protonic defects. The strong O-H stretch band, 2500-3500 cm-1, in the IR absorbance spectrum also clearly manifests the presence of significant levels of protons in the hydrated material. Proton conductivity was investigated on prehydrated (under dry Ar) and as-prepared (under wet Ar) samples. The heating cycle of the prehydrated sample showed higher proton conductivity compared to the cooling cycle, especially in the intermediate temperature range (150-550°C). Finally, comparison with data for Ba Zr0.9 Yb0.1 O3-δ revealed that the more heavily doped sample showed higher proton conductivity compared to the more lightly doped sample. © 2008 The Electrochemical Society.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Ahmed, Istaq, 19 ...
-
Knee, Christophe ...
-
Eriksson, Sten, ...
-
Ahlberg, Elisabe ...
-
Karlsson, Maths, ...
-
Matic, Aleksanda ...
-
visa fler...
-
Börjesson, Lars, ...
-
visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
och Annan materialte ...
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Kemi
- Artiklar i publikationen
-
Journal of the E ...
- Av lärosätet
-
Chalmers tekniska högskola
-
Göteborgs universitet