Use of Nickel Oxide as a Catalyst for Tar Elimination in a Chemical-Looping Reforming Reactor Operated with Biomass Producer Gas

• A secondary tar-cleaning process based on Chemical-Looping Reforming (CLR) was investigated for upgrading biomass producer gas, derived from the Chalmers University of Technology 2-4 MW indirect gasifier. The experiments were conducted in a bench-scale CLR reactor using a manufactured nickel oxide (NiO) catalyst. Although Ni is a well-documented and efficient steam-reforming catalyst, it is susceptible to rapid deactivation under tar-rich conditions. The aim of this study was to explore the advantages of CLR as a gas-cleaning application, a process which offers continuous regeneration of the carbon deposits on catalysts. The tar-reforming performance of this Ni material and its influence on the gas composition and in particular its potential to increase the H2/CO ratio, were studied. The system was tested at reforming temperatures that ranged from 700°C to 880°C and at oxygen concentrations of 1.0% and 2.2% in the inlet feed to regenerator section. The results confirm the strong ability of the catalyst to reform tars. Higher process temperatures clearly promoted tar conversion, with 96% overall conversion at 880°C (99% if benzene is excluded), as compared with 45% conversion at 700°C. The hydrogen production was favored when temperature was raised. Though, a maximum ratio H2/CO of 2.2 was observed at 750°C. Finally, no time-on-stream deactivation of the catalyst in the CLR was observed during the test, which lasted almost 7 hours.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Maskinteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering (hsv//eng)

NATURVETENSKAP  -- Kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences (hsv//eng)

Nyckelord

Tars

Chemical-Looping Reforming

Catalytic Gas Cleaning

Circulating Fluidized Beds

Biomass Gas Upgrading

Nickel Oxide Catalyst

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)