Dielectric Properties and Partial Discharge Endurance of Polypropylene- Silica Nanocomposite
-
- Takala, M. (författare)
- Tammerfors tekniska universitet,Tampere University of Technology
-
- Ranta, H. (författare)
- Tammerfors tekniska universitet,Tampere University of Technology
-
- Navalainen, P. (författare)
- Tammerfors tekniska universitet,Tampere University of Technology
-
visa fler...
-
- Pakonen, P. (författare)
- Tammerfors tekniska universitet,Tampere University of Technology
-
- Pelto, J. (författare)
- Teknologian Tutkimuskeskus (VTT),Technical Research Centre of Finland (VTT)
-
- Karttunen, M. (författare)
- Teknologian Tutkimuskeskus (VTT),Technical Research Centre of Finland (VTT)
-
- Virtanen, S. (författare)
- Jyväskylän Yliopisto,University of Jyväskylä
-
- Koivu, V. (författare)
- Jyväskylän Yliopisto,University of Jyväskylä
-
- Pettersson, M. (författare)
- Jyväskylän Yliopisto,University of Jyväskylä
-
- Sonerud, Björn, 1979 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Kannus, K (författare)
- Tammerfors tekniska universitet,Tampere University of Technology
-
visa färre...
-
(creator_code:org_t)
- 2010
- 2010
- Engelska.
-
Ingår i: IEEE Transactions on Dielectrics and Electrical Insulation. - 1558-4135 .- 1070-9878. ; 17:4, s. 1259-1267
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://research.cha...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- This paper presents the results of the dielectric properties and partial discharge endurance measurements conducted on polypropylene (PP)-silica nanocomposite. The material compounds were analyzed with micro-Raman spectroscopy, X-ray tomography and transmission electron microscopy (TEM). ac and dc breakdown strength of the materials was measured. Dielectric response, capacitance and loss factor of the film samples were measured as a function of temperature and frequency. Partial discharge (PD) endurance of the reference PP and PP Silica nanocomposite was studied as a function of ac voltage. Material surfaces were analyzed after PD stress with optical microscopy. All dielectric measurements were done for oriented thin films with a thickness of 11-23 μm. The results were analyzed statistically to determine the effects of the additive on the properties of PP. The paper discusses the potential of PP Silica nanocomposite with a view to high voltage applications, especially power capac itors. © 2010 IEEE.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Elektroteknik och elektronik -- Annan elektroteknik och elektronik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Electrical Engineering, Electronic Engineering, Information Engineering -- Other Electrical Engineering, Electronic Engineering, Information Engineering (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Takala, M.
-
Ranta, H.
-
Navalainen, P.
-
Pakonen, P.
-
Pelto, J.
-
Karttunen, M.
-
visa fler...
-
Virtanen, S.
-
Koivu, V.
-
Pettersson, M.
-
Sonerud, Björn, ...
-
Kannus, K
-
visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Elektroteknik oc ...
-
och Annan elektrotek ...
- Artiklar i publikationen
-
IEEE Transaction ...
- Av lärosätet
-
Chalmers tekniska högskola