Sökning: onr:"swepub:oai:research.chalmers.se:d4462e3d-bcee-43f8-9491-c13347b0d6af" >
Structural study an...
Structural study and proton conductivity in Yb-doped BaZrO3
-
- Ahmed, Istaq, 1972 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Eriksson, Sten, 1958 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Ahlberg, Elisabet, 1952 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för kemi,Department of Chemistry
-
visa fler...
-
- Knee, Christopher, 1973 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för kemi,Department of Chemistry
-
- Götlind, Helena, 1978 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Johansson, Lars-Gunnar, 1952 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Karlsson, Maths, 1978 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Matic, Aleksandar, 1968 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Börjesson, Lars, 1957 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- 2007
- 2007
- Engelska.
-
Ingår i: Solid State Ionics. - 0167-2738. ; 178:(7-10), s. 515-520
- Relaterad länk:
-
https://research.cha...
-
visa fler...
-
https://gup.ub.gu.se...
-
visa färre...
Abstract
Ämnesord
Stäng
- Traditional solid state sintering has been used to prepare the perovskite BaZr0.9Yb0.1O3-delta. Analysis of X-ray powder diffraction data shows that an increase of the unit cell parameter, a, was observed compared to undoped BaZrO3. Rietveld analysis of room temperature neutron powder diffraction data confirmed cubic symmetry (space group Pm-3m). Dynamic thermogravimetric analysis (TGA) indicates that the hydration process occurs below 200 degrees C. The strong O-H stretch band, 2500-3500 cm(-1), in the infrared absorbance spectrum clearly manifests the presence of protons in the hydrated material. Proton conductivity was investigated on hydrated and as-prepared samples under dry and wet atmospheres, respectively. Keywords: X-ray diffraction; neutron diffraction; Rietveld refinement; proton conductor; perovskite
Ämnesord
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
- NATURVETENSKAP -- Fysik -- Den kondenserade materiens fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences -- Condensed Matter Physics (hsv//eng)
Nyckelord
- BACEO3
- POWDER DIFFRACTION
- NEUTRON
- STRONTIUM
- PEROVSKITE-TYPE OXIDES
- CONDUCTORS
- CERATE
- PEROVSKITE-TYPE OXIDES; POWDER DIFFRACTION; CONDUCTORS; STRONTIUM; NEUTRON; BACEO3; CERATE
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Ahmed, Istaq, 19 ...
-
Eriksson, Sten, ...
-
Ahlberg, Elisabe ...
-
Knee, Christophe ...
-
Götlind, Helena, ...
-
Johansson, Lars- ...
-
visa fler...
-
Karlsson, Maths, ...
-
Matic, Aleksanda ...
-
Börjesson, Lars, ...
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Kemi
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Fysik
-
och Den kondenserade ...
- Artiklar i publikationen
-
Solid State Ioni ...
- Av lärosätet
-
Chalmers tekniska högskola
-
Göteborgs universitet