Solid solution softening at room temperature and hardening at elevated temperatures: a case by minor Mn addition in a (HfNbTi) 85 Mo 15 refractory high entropy alloy
- Artikel/kapitelEngelska2023
Förlag, utgivningsår, omfång ...
-
2023
-
electronicrdacarrier
Nummerbeteckningar
-
LIBRIS-ID:oai:research.chalmers.se:f3805e6b-0134-482e-9b19-cc0267a02578
-
https://doi.org/10.1088/2053-1591/ad068cDOI
-
https://research.chalmers.se/publication/538462URI
Kompletterande språkuppgifter
-
Språk:engelska
-
Sammanfattning på:engelska
Ingår i deldatabas
Klassifikation
-
Ämneskategori:art swepub-publicationtype
-
Ämneskategori:ref swepub-contenttype
Anmärkningar
-
To address the conflict between room-temperature (RT) ductility and high-temperature (HT) strength in single phase bcc-structured refractory high entropy alloys, here we propose to use minor alloying to achieve solid solution softening at RT and simultaneously, solid solution hardening at HT. Our strategy was manifested by minor Mn additions in a RT brittle (HfNbTi)85Mo15 refractory high entropy alloy, where nominal Mn additions ranging from 2 at. % down to 0.03 at. % were seen to soften the base (HfNbTi)85Mo15 alloy at RT, while to harden the base alloy at the temperature range from 400 to 800 °C. The yield stress in all studied alloys showed a three-stage pattern, characterized by a temperature dependent stage at temperatures below 400 °C, followed by a temperature independent stage at intermediate temperatures ranging from 400 to 800 °C, and finally another temperature dependent stage at temperatures higher than 800 °C. The mechanisms for solid solution softening and solid solution hardening in single phase bcc-structured refractory high entropy alloys were discussed, together with their temperature dependence.
Ämnesord och genrebeteckningar
Biuppslag (personer, institutioner, konferenser, titlar ...)
-
Ding, MaoShenzhen University
(författare)
-
Hu, Q.Jiangxi Academy of Sciences
(författare)
-
Liu, Z. Y.Shenzhen University
(författare)
-
Mao, H. H.
(författare)
-
Guo, Sheng,1981Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)shengg
(författare)
-
Chalmers tekniska högskolaShenzhen University
(creator_code:org_t)
Sammanhörande titlar
-
Ingår i:Materials Research Express10:112053-1591
Internetlänk
Hitta via bibliotek
Till lärosätets databas