1. |
- Alnegren, Patrik, 1988, et al.
(author)
-
Inhibiting chromium evaporation and oxide scale growth on SOFC metallic interconnects by nano coatings
- 2014
-
In: 20th World Hydrogen Energy Conference, WHEC 2014. - 9780000000002 ; 1:2014
-
Conference paper (peer-reviewed)abstract
- High chromium ferritic steel is today the most commonly considered material for SOFC interconnectors due to many desirable properties, such as matching thermal expansion coefficient with other cell components but most importantly better machinability and price compared to ceramic alternatives. Yet there are some obstacles that need to be addressed before long term stability of a ferritic steel interconnector based fuel cell stack can be realized. First of all the electrical conductivity needs to remain high throughout the fuel cell stack operating life time and thus the formed oxide layers need to be electrically conductive and thin. Secondly, volatilization of chromium from the oxide scale of metallic interconnects causes rapid degradation due cathode poisoning. In the current study both oxidation and chromium evaporation of ferritic steel substrates are investigated in controlled atmospheres that simulates the environments of an operating SOFC stack. Samples coated with nanometer scale dual coatings of Co and Ce were tested. The dual coating substantially increased the performance of the ferritic substrates by i) significantly reducing oxidation rate, ii) increasing scale adherence and iii) diminishing chromium evaporation by 90 % via the formation of a Co-Mn-spinel cap layer.
|
|
2. |
- Grolig, Jan Gustav, 1986, et al.
(author)
-
Copper based conversion coatings on ferritic stainless strip steel as solid oxide fuel cell interconnects: Oxidation performance and chromium evaporation
- 2013
-
In: ECS Transactions. - : The Electrochemical Society. - 1938-5862 .- 1938-6737. ; 57:1, s. 2339-2347
-
Conference paper (peer-reviewed)abstract
- Ferritic stainless steels such as Crofer 22 H or Sanergy HT have been proven to be effective interconnect materials when additionally coated. These coatings, mainly based on cobalt spinels, successfully prevent chromium evaporation and are stable for long exposure times. A new approach is using copper based spinel coatings which are promising concerning price, conductivity and stability. This investigation is dedicated to a selection of copper spinel conversion coatings, their stability and ability to prevent chromium evaporation. Chromium release was monitored in humidified air (at 850 °C) using the denuder technique. The coatings were post analysed utilizing electron microscopy.
|
|
3. |
- Falk Windisch, Hannes, 1984, et al.
(author)
-
Chromium vaporization from mechanically deformed pre-coated interconnects in Solid Oxide Fuel Cells
- 2015
-
In: Journal of Power Sources. - : Elsevier BV. - 0378-7753. ; 297, s. 217-223
-
Journal article (peer-reviewed)abstract
- Cathode poisoning, associated with Cr evaporation from interconnect material, is one of the most important degradation mechanisms in Solid Oxide Fuel Cells when Cr2O3-forming steels are used as the interconnect material. Coating these steels with a thin Co layer has proven to decrease Cr vaporization. To reduce production costs, it is suggested that thin metallic PVD coatings be applied to each steel strip before pressing the material into interconnect shape. This process would enable high volume production without the need for an extra post-coating step. However, when the pre-coated material is mechanically deformed, cracks may form and lower the quality of the coating. In the present study, Chromium volatilization is measured in an air-3% H2O environment at 850 C for 336 h. Three materials coated with 600 nm Co are investigated and compared to an uncoated material. The effect of deformation is investigated on real interconnects. Microscopy observations reveal the presence of cracks in the order of several μm on the deformed pre-coated steel. However, upon exposure, the cracks can heal and form a continuous surface oxide rich in Co and Mn. As an effect of the rapid healing, no increase in Cr vaporization is measured for the pre-coated material.
|
|
4. |
- Falk Windisch, Hannes, 1984, et al.
(author)
-
Co- and Ce/Co-coated ferritic stainless steel as interconnect material for Intermediate Temperature Solid Oxide Fuel Cells
- 2017
-
In: Journal of Power Sources. - : Elsevier BV. - 0378-7753. ; 343, s. 1-10
-
Journal article (peer-reviewed)abstract
- Chromium species volatilization, oxide scale growth, and electrical scale resistance were studied at 650 and 750 °C for thin metallic Co- and Ce/Co-coated steels intended to be utilized as the interconnect material in Intermediate Temperature Solid Oxide Fuel Cells (IT-SOFC). Mass gain was recorded to follow oxidation kinetics, chromium evaporation was measured using the denuder technique and Area Specific Resistance (ASR) measurements were carried out on 500 h pre-exposed samples. The microstructure of thermally grown oxide scales was characterized using Scanning Electron Microscopy (SEM), Scanning Transmission Electron Microscopy (STEM), and Energy Dispersive X-Ray Analysis (EDX). The findings of this study show that a decrease in temperature not only leads to thinner oxide scales and less Cr vaporization but also to a significant change in the chemical composition of the oxide scale. Very low ASR values (below 10 m? cm2) were measured for both Co- and Ce/Co-coated steel at 650 and 750 °C, indicating that the observed change in the chemical composition of the Co spinel does not have any noticeable influence on the ASR. Instead it is suggested that the Cr2O3 scale is expected to be the main contributor to the ASR, even at temperatures as low as 650 °C.
|
|
5. |
- Falk Windisch, Hannes, 1984, et al.
(author)
-
Determination of the oxide scale growth mechanism using 18O-tracer experiments in combination with Transmission Electron Microscopy and nanoscale Secondary Ion Mass Spectrometry
- 2018
-
In: Materials Characterization. - : Elsevier BV. - 1044-5803. ; 136, s. 128-133
-
Journal article (peer-reviewed)abstract
- Two-stage 18 O 2 / 16 O 2 exposures can be used to investigate the effect that alloying elements, secondary phases, or surface treatments have on the high temperature oxidation behaviour of certain materials. During subsequent exposures to 16 O 2 - and 18 O 2 -rich atmospheres, 16 O- and 18 O-rich layers are formed. Analysis of the layers using Seco ndary Ion Mass Spectrometry (SIMS) depth profiling allows for conclusions to be drawn about the oxide scale growth mechanism. The conclusions are, however, not entirely unambiguous due to the limited lateral resolution of the technology. Rough surface topography and the thickness variation of the oxide scale over the analysed volume add to the ambiguity of the findings. In this study, an Fe-20%Cr alloy was exposed to both 18 O- and 16 O-rich environments at 850 °C. Two methods were used to analyse the thermally grown Cr 2 O 3 scale: (1) traditional SIMS depth profiling and (2) preparation of a cross-sectional lamellae for Transmission Electron Microscopy (TEM), which, subsequently, was analysed in a NanoSIMS. The NanoSIMS 16 O and 18 O elemental maps were then superimposed on the TEM image. In comparison with traditional SIMS depth profiling, the nanoSIMS elemental maps reveal detailed information about local oxide growth in different parts of an oxide scale. Moreover, a clear 16 O/ 18 O interface can be seen in the nanoSIMS maps, which is not the case in the sputter depth profiles. The findings of this study show that the aforementioned issues associated with sputter depth profiling can be eliminated by mapping a cross-section of an oxide scale using high resolution nanoSIMS.
|
|
6. |
- Falk Windisch, Hannes, 1984, et al.
(author)
-
Influence of chromium evaporation and oxidation on interconnect steels at 650-850°C
- 2013
-
In: ECS Transactions. - : The Electrochemical Society. - 1938-5862 .- 1938-6737. ; 57:1, s. 2225-2233
-
Conference paper (peer-reviewed)abstract
- Chromium evaporation and oxide scale growth are two important degradation mechanisms in SOFCs when chromia-forming alloys are used as the interconnect material. In this paper the influence of temperature on both mechanisms were studied. Isothermal exposures were carried out for 24, 168 and 500h at 650, 750 and 850°C in an air-3%H2O atmosphere. In the second part uncoated and metallic nano-coated samples were exposed for 3000h. This study clearly points out the relevance of Cr-evaporation at reduced temperatures and the importance of high quality coatings not only to protect the cell from cathode poisoning but also to reduce the risk of Cr-depletion within the interconnect steel.
|
|
7. |
- Falk Windisch, Hannes, 1984, et al.
(author)
-
Metallic thin-film Co- and Ce/Co-coated steels as interconnect material in IT-SOFC
- 2017
-
In: ECS Transactions. - : The Electrochemical Society. - 1938-5862 .- 1938-6737. - 9781607685395 ; 78:1, s. 1607-1614
-
Conference paper (peer-reviewed)abstract
- Cr vaporization, oxide scale growth, and the electrical scale resistance (ASR) were studied at 650°C on coated interconnects intended for IT-SOFC applications. The custom-made SOFC interconnect steel Sanergy HT was coated with thin-film Co- and Ce/Co-coatings and compared to the less expensive substrate steel AISI 441 which was coated with Ce/Co and a 15-20 μm thick commercial MCO-coating. All coated materials mitigated Cr vaporization, and due to the very thin chromia scales formed at the low exposure temperature, ASR values below 10 mΩcm 2 were measured for all materials after 500 h at 650°C. The results in this study show that thin-film metallic Co- and Ce/Co-coated steels show excellent properties as interconnect materials for IT-SOFCs. Thick MCO-coatings can also be used at low temperatures; however, the coating method might be a critical issue for lowtemperature applications.
|
|
8. |
- Falk Windisch, Hannes, 1984, et al.
(author)
-
Pre-coated Ce/Co-coated steel: Mitigating Cr vaporization, increasing corrosion resistance at competitive cost
- 2015
-
In: ECS Transactions. - : The Electrochemical Society. - 1938-5862 .- 1938-6737. - 9781607685395 ; 68:1, s. 1617-1623
-
Conference paper (peer-reviewed)abstract
- Cr vaporization and oxide scale growth are probably the two most detrimental degradation mechanisms associated to Cr2O3-forming alloys as interconnect material in SOFC. Both issues can be improved by the application of coatings. However, the use of coatings increase material cost. To reduce coating costs it is suggested that large amounts of steel can be coated before shaping the pre-coated material into an interconnect. The present study investigates the effectiveness of thin Ce and Co coatings on the cost effective steel AISI 441 with respect to Cr vaporization and corrosion resistance. Furthermore, the effect of mechanical deformation of the coated steel is examined. The results revealed that when the pre-coated steel is deformed, large cracks are formed. However, upon exposure those cracks can heal forming a continuous surface oxide rich in Co and Mn. As an effect of the rapid healing, no increase in Cr vaporization was measured.
|
|
9. |
- Falk Windisch, Hannes, 1984, et al.
(author)
-
The Effect of Metallic Co-Coating Thickness on Ferritic Stainless Steels Intended for Use as Interconnect Material in Intermediate Temperature Solid Oxide Fuel Cells
- 2018
-
In: Oxidation of Metals. - : Springer Science and Business Media LLC. - 1573-4889 .- 0030-770X. ; 89:1-2, s. 233-250
-
Journal article (peer-reviewed)abstract
- The effect of metallic Co-coating thickness on ferritic stainless steels is investigated. This material is suggested to be used as interconnect material in intermediate temperature solid oxide fuel cells. Uncoated, 200-, 600-, 1000-, and 1500-nm Co-coated Sanergy HT is isothermally exposed for up to 500 h in air at 650 A degrees C. Mass gain is recorded to follow oxidation kinetics, and area-specific resistance (ASR) measurements are conducted on samples exposed for 168 and 500 h. The microstructure of the thermally grown oxide scales is characterized utilizing scanning electron microscopy and energy-dispersive X-ray analysis on broad ion beam-milled cross sections. A clear increase in ASR as a function of Co-coating thickness is observed. However, the increase in ASR, as an effect of a thicker Co-coating, is correlated with thicker (Cr,Fe)(2)O-3 scales formed on these materials and not to an increase in Co spinel top layer thickness.
|
|
10. |
- Falk Windisch, Hannes, 1984, et al.
(author)
-
The effect of temperature on chromium vaporization and oxide scale growth on interconnect steels for Solid Oxide Fuel Cells
- 2015
-
In: Journal of Power Sources. - : Elsevier BV. - 0378-7753. ; 287, s. 25-35
-
Journal article (peer-reviewed)abstract
- Chromium vaporization and oxide scale growth are probably the two most important degradation mechanisms associated with the interconnect in Solid Oxide Fuel Cells (SOFCs) when Cr2O3-forming alloys are used as the interconnect material. This study examines the influence of temperature on both mechanisms. Two commercially available steels; Crofer 22 H and Sanergy HT, were isothermally exposed at 650, 750 and 850 °C in an air-3% H2O atmosphere with a high flow rate. Volatile chromium species were collected using the denuder technique. The microstructure of thermally grown oxide scales was characterized using Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray Analysis (EDX) and X-Ray Diffraction (XRD). The findings of this study show that although Cr evaporation is reduced with lower temperature, its relative importance compared to oxide scale growth is greater.
|
|