  • Preparation of 30 mol.% Y-doped hafnia (Hf0.7Y0.3O2-delta) using a modified solid-state reaction method
  • 2015
  • Ingår i: Ceramics International. - : Elsevier BV. - 0272-8842 .- 1873-3956. ; 41:2, s. 2611-2615
  • Tidskriftsartikel (refereegranskat)abstract
    • A pure and well-crystallized Hf0.7Y0.3O2-delta (YSH) powder was synthesized using a modified solid-state reaction method. Water-based milling and freeze drying process were implemented to facilitate powder synthesis and final densification process. The improved powder performance, in aspects of phase development and sintering behaviour, was investigated by systematic comparison between different powder processing procedures. Dense YSH ceramic material with a relative density of 0.975 was successfully obtained using conventional sintering at 1650 degrees C for 10 h. XRD, SEM and EDS were employed to characterize the synthesized powder and dense YSH ceramics. Dense YSH ceramic possesses a fluorite cubic structure with an a value of 5.1406 angstrom, and the ionic radius of Y3+ in YSH was determined to be 0.1006 nm.
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-1 av 1
Typ av publikation
tidskriftsartikel (1)
Typ av innehåll
refereegranskat (1)
Författare/redaktör
Jönsson, Pär G. (1)
Zhao, Zhe (1)
Bu, Junfu (1)
Lärosäte
Kungliga Tekniska Högskolan (1)
Språk
Engelska (1)
Forskningsämne (UKÄ/SCB)
Teknik (1)
År
2015 (1)

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy