  • Glauser, T., et al. (författare)
  • Toughening of electron-beam cured acrylate resins
  • 2000
  • Ingår i: Macromolecular materials and engineering. - 1438-7492 .- 1439-2054. ; 280:08-jul, s. 20-25
  • Tidskriftsartikel (refereegranskat)abstract
    • The aim of this study was to improve the toughness of EB-cured acrylate thermost resins by using hyperbranched aliphatic polyesters as additives to obtain a liquid-liquid phase-separated resin. The hyperbranched polyester can be considered as a hydroxyl functional scaffold, on which functional groups were reacted by control phase separation and crosslinking. Alkyl chains of different lengths attached to the scaffold controlled phase separation. The amount of crosslinking within the rubbery particle and between the particles and the matrix was set by the percentage of methacrylate groups. A good phase separation was obtained; therefore, T-g decreased only slightly compared to the pure acrylate. The K-IC value of the cured resins was increased by 30%. The phase-separated resins showed stability with time and no significant increase in particle size was noticed after 18 months.
  •  
Skapa referenser, mejla, bekava och länka
  • Resultat 1-1 av 1
Typ av publikation
tidskriftsartikel (1)
Typ av innehåll
refereegranskat (1)
Författare/redaktör
Hult, Anders (1)
Berglund, Lars A. (1)
Johansson, Mats K. G ... (1)
Glauser, T (1)
Kornmann, X. (1)
Lärosäte
Kungliga Tekniska Högskolan (1)
Luleå tekniska universitet (1)
Språk
Engelska (1)
Forskningsämne (UKÄ/SCB)
Teknik (1)
År
2000 (1)

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy