- Aguilar-Sanchez, Andrea, et al.
(författare)
-
Waterborne nanocellulose coatings for improving the antifouling and antibacterial properties of polyethersulfone membranes
- 2021
-
Ingår i: Journal of Membrane Science. - : Elsevier BV. - 0376-7388 .- 1873-3123. ; 620
-
Tidskriftsartikel (refereegranskat)abstract
- This article presents a waterborne nanocellulose coating process to change the surface characteristics and mitigate fouling of commercially available polyethersulfone (PES) microfiltration membranes. An extensive comparative study between nanoporous and nano-textured layers composed of cellulose nanocrystals (CNC) or TEMPO-oxidized cellulose nanofibrils (T-CNF), which were coated on the PES membrane by taking advantage of the electrostatic interactions between the PES substrate, a polyallylamine hydrochloride (PAHC1) anchoring layer, and the nanocellulose functional layer. Coated PES membranes exhibited decreased surface roughness and pore sizes as well as rejection of compounds with a M-w above 150 kDa, while the water permeability and mechanical properties of remained largely unaffected. The coatings improved the wettability as confirmed by a reduction of the contact angle by up to 52% and exhibited a higher negative surface charge compared to the uncoated membranes over a pH range of 4-8. A significant reduction in organic fouling was observed for the coated membranes demonstrated by bovine serum albumin (BSA) adsorption studies on T-CNF and CNC surfaces using Quartz Crystal Microbalance with Dissipation monitoring (QCM-D), UV-vis spectroscopy and FTIR mapping after exposing the membranes to dynamic adsorption of BSA. The T-CNF coating exhibited effective antibacterial action against Escherichia coli (E. coli) attributed to the pH reduction effect induced by the carboxyl groups; while CNC coatings did not show this property. This work demonstrates a simple, green, and easy-to-scale layer-by-layer coating process to tune the membrane rejection and to improve antifouling and antibacterial properties of commercially available membranes.
|
|