1.	Konofaos, N., et al. (författare) Electrical characterisation of SrTiO3/Si interfaces 2002 Ingår i: Journal of Non-Crystalline Solids. - 0022-3093 .- 1873-4812. ; 303:1, s. 185-189 Tidskriftsartikel (refereegranskat)abstract Deposition of SrTiO3 (STO) thin films by ultra-high vacuum rf magnetron sputtering was performed in order to produce high-quality STO/p-Si (1 0 0) interfaces and STO insulator layers with high dielectric constants. The deposition temperatures were in the range from room temperature to 550 °C. Capacitance-voltage (C-V) and conductance-frequency measurements showed that the dielectric constant of the films ranges from 55 to 120. C-V measurements on Al/STO/p-Si structures clearly revealed the creation of metal-insulator-semiconductor diodes. The interface state densities (Dit) at the STO/p-Si interfaces were obtained from admittance spectroscopy measurements. The samples deposited at lower temperatures revealed values of Dit between 2 × 1011 and 3.5 × 1012 eV-1 cm-2 while the higher temperature deposited samples had a higher Dit ranging between 1 × 1011 and 1 × 1013 eV-1 cm-2. The above results were also well correlated to X-ray diffraction measurements, Rutherford backscattering spectroscopy, and spectroscopic ellipsometry. © 2002 Elsevier Science Ltd. All rights reserved.

Konofaos, N., et al. (författare)
Electrical characterisation of SrTiO3/Si interfaces
2002
Ingår i: Journal of Non-Crystalline Solids. - 0022-3093 .- 1873-4812. ; 303:1, s. 185-189
Tidskriftsartikel (refereegranskat)abstract
- Deposition of SrTiO3 (STO) thin films by ultra-high vacuum rf magnetron sputtering was performed in order to produce high-quality STO/p-Si (1 0 0) interfaces and STO insulator layers with high dielectric constants. The deposition temperatures were in the range from room temperature to 550 °C. Capacitance-voltage (C-V) and conductance-frequency measurements showed that the dielectric constant of the films ranges from 55 to 120. C-V measurements on Al/STO/p-Si structures clearly revealed the creation of metal-insulator-semiconductor diodes. The interface state densities (Dit) at the STO/p-Si interfaces were obtained from admittance spectroscopy measurements. The samples deposited at lower temperatures revealed values of Dit between 2 × 1011 and 3.5 × 1012 eV-1 cm-2 while the higher temperature deposited samples had a higher Dit ranging between 1 × 1011 and 1 × 1013 eV-1 cm-2. The above results were also well correlated to X-ray diffraction measurements, Rutherford backscattering spectroscopy, and spectroscopic ellipsometry. © 2002 Elsevier Science Ltd. All rights reserved.

Träfflista för sökning "id:"swepub:oai:DiVA.org:liu-47021" "